Safrene® F 7650
- Chemical Family
- PolyethylenesPolyolefins
Safrene® F 7650 High Density Polyethylene Resin is a bimodal medium molecular weight blow molding grade with good processing properties. It exhibits good impact strength and excellent environmental stresscrack resistance. Safrene® F 7650 High Density Polyethylene Resin is recommended for general purpose applications up to 20 liter in volume.
Product families
Applications
- Industrial & Transport Packaging
Product Families
- Polyolefins
Other characteristics
- Brand
- Safrene
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 0.33 - 0.33 g/10 min
- Processing Methods
- Blow Molding
- Markets
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
Bimodal Molecular Weight Distribution; Food Contact Acceptable; General Purpose; Good Environmental Stress Crack Resistance (ESCR); Good Impact Strength; Good Processability
- Food Contact Compliance
Safrene® F 7650 High Density Polyethylene Resin should comply with Commission Regulation (EU) No 10/2011 and with U.S. FDA 21 CFR 177.1520(c)3.2a food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. The purchaser remains responsible for determining whether the use complies with all relevant regulations.
- Certifications and Compliance
- FDA 21 CFR 177.1520
- Regulation (EU) No. 10/2011 (PIM)
- Plastics and Elastomers End Uses
- Containers
- General Purpose
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Blow Molding
Technical data
Table 1 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 62 | Shore D | ISO 868 |
| Tensile Yield | 23 | MPa | ISO 527 |
| Ultimate Tensile | 36 | MPa | ISO 527 |
| Ultimate Elongation | min. 600 | % | ISO 527 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Environmental Stress-Crack Resistance | min. 1000 | Hours | ASTM D 1693 |
| Charpy Notched Impact Strength (23 °C) | 11 | kJ/m2 | ISO 179 |
| Charpy Notched Impact Strength (-30 °C) | 8 | kJ/m2 | ISO 179 |
Table 2 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (190 °C/ 5 kg) | 1.7 | g/10min | ISO 1133 |
| Melt Flow Rate (190 °C/ 2.16 kg) | 0.33 | g/10min | ISO 1133 |
| Density | 0.95 | g/cm3 | ISO 1183 |
Table 3 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Point A (10N) | 126 | °C | ISO 306/A |
| Vicat Softening Point B (50N) | 70 | °C | ISO 306/B |
| Crystalline Melting Range | 130-133 | °C | ISO 3146 |