Safron® H504 - 12M
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Safron® H504 - 12M polypropylene resin is recommended for the spinning of staple fiber in the range 2 – 25 denier. It is also used for the manufacture of Bulk Continuous Filament (BCF) yarns. Safron® H504-12M Polypropylene Resin is a medium to high flow injection molding grade for applications where rigidity and fast cycle times are essential.
Product families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Safripol Safron
- Polymer Name
- Polypropylene Homopolymer (HPP)
- Melt Flow Index
- 12.0 - 12.0 g/10 min
- Processing Methods
- Extrusion, Injection Molding
- Markets
- Building & Construction
- Consumer Goods
- Industrial
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Food Contact Acceptable
- Food Contact Compliance
Safrene® H504 - 12M Polyethylene Resin should comply with Commission Regulation (EU) No 10/2011 and with U.S. FDA 21 CFR 177.1520(c)3.2a food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. The purchaser remains responsible for determining whether the use complies with all relevant regulations.
- Certifications and Compliance
- FDA 21 CFR 177.1520
- Regulation (EU) No. 10/2011 (PIM)
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield | 30 | MPa | ISO 527 |
| Elongation at Yield | 7.5 | % | ISO 527 |
| Flexural Modulus | 1360 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23 °C) | 2.3 | kJ/m2 | ISO 179 |
Table 2 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (230 °C/ 2.16 kg) | 12 | g/10min | ISO 1133 |
| Density | 0.9 | g/cm3 | ISO 1183 |
Table 3 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT A (1.8 MPa) | 55 | °C | ISO 75/A |
| Heat Deflection Temperature - HDT B (0.45 MPa) | 83 | °C | ISO 75/B |
| Vicat Softening Point B (50 N) | 85 | °C | ISO 306/B |