Safron® C142 - 01N
- Chemical Family
- PolyolefinsPolypropylenes (PP)
Safron® C142 - 01N is a polypropylene resin which is a nucleated high impact copolymer especially suited for twin walled sheet applications. Its good compressive strength combined with flexibility for easy stamping out of complex shapes, renders it useful for a wide variety of applications. It is also suitable for profile extrusion. Safron® C142-01N Polypropylene Resin can also be used for the injection molding of technical parts requiring exceptional toughness, especially at low temperatures.
Product families
Applications
- Tooling & Moldmaking
Product Families
- Polyolefins
Other characteristics
- Brand
- Safripol Safron
- Polymer Name
- Polypropylene Impact Copolymer (ICP)
- Melt Flow Index
- 1.4 - 1.4 g/10 min
- Processing Methods
- Extrusion, Injection Molding
- Markets
- Industrial
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Food Contact Acceptable
- General Purpose
- Good Compressive Strength
- Good Impact Strength
- Good Toughness
- High Flexibility
- Food Contact Compliance
Safrene® C142 - 01N Polyethylene Resin should comply with Commission Regulation (EU) No 10/2011 and with U.S. FDA 21 CFR 177.1520(c)3.2a food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. The purchaser remains responsible for determining whether the use complies with all relevant regulations.
- Certifications and Compliance
- FDA 21 CFR 177.1520
- Regulation (EU) No. 10/2011 (PIM)
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 3
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (230 °C/ 2.16 kg) | 1.4 | g/10min | ISO 1133 |
| Density | 0.91 | g/cm3 | ISO 1183 |
Table 2 of 3
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield | 26 | MPa | ISO 527 |
| Elongation at Yield | 7 | % | ISO 527 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Charpy Notched Impact Strength (0 °C) | 7 | kJ/m2 | ISO 179 |
| Charpy Notched Impact Strength (-20 °C) | 5 | kJ/m2 | ISO 179 |
Table 3 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature - HDT A (1.8 MPa) | 52 | °C | ISO 75/A |
| Heat Deflection Temperature - HDT B (0.45 MPa) | 74 | °C | ISO 75/B |
| Vicat Softening Point B (50 N) | 71 | °C | ISO 306/B |