Safrene® C 7260
- Chemical Family
- PolyethylenesPolyolefins
Safrene® C 7260 High Density Polyethylene Resin is an injection molding grade with high flow characteristics, good mechanical strength and high stiffness combined with low distortion tendency. It is especially suited for crates and industrial containers.
Product families
Applications
Printing & Packaging — Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Product Families
Plastics — Basic Thermoplastics
- Polyolefins
Other characteristics
- Brand
- Safrene
- Polymer Name
- High Density Polyethylene (HDPE)
- Melt Flow Index
- 7.0 - 7.0 g/10 min
- Processing Methods
- Injection Molding
- Markets
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Excellent Mechanical Strength
- Food Contact Acceptable
- Good Processability
- High Flow
- High Stiffness
- Food Contact Compliance
Safrene® C 7260 High Density Polyethylene Resin should comply with Commission Regulation (EU) No 10/2011 and with U.S. FDA 21 CFR 177.1520(c)3.2a food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. The purchaser remains responsible for determining whether the use complies with all relevant regulations.
- Certifications and Compliance
- FDA 21 CFR 177.1520
- Regulation (EU) No. 10/2011 (PIM)
- Plastics and Elastomers End Uses
- Caps
- Closures
- Containers
- Crates
- Pipes
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 3
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melt Flow Rate (190 °C/ 5 kg) | 23 | g/10min | ISO 1133 |
| Melt Flow Rate (190 °C/ 2.16 kg) | 7 | g/10min | ISO 1133 |
| Density | 0.958 | g/cm3 | ISO 1133 |
| Spiral Flow Test | 47 | % | Internal |
Table 2 of 3
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 65 | Shore D | ISO 868 |
| Tensile Stress at Yield | 32 | MPa | ISO 527 |
| Tensile Stress at Break | 20 | MPa | ISO 527 |
| Tensile Strain at Yield | 10 | % | ISO 527 |
| Tensile Strain at Break | min. 800 | % | ISO 527 |
| Flexural Modulus | 1450 | MPa | ISO 178 |
| Charpy Notched Impact Strength (23 °C) | 4 | kJ/m2 | ISO 179 |
| Charpy Notched Impact Strength (-30 °C) | 4 | kJ/m2 | ISO 179 |
Table 3 of 3
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Point A (10N) | 127 | °C | ISO 306/A |
| Vicat Softening Point B (50N) | 72 | °C | ISO 306/B |
| Crystalline Melting Range | 130 - 133 | °C | ISO 3146 |