BindEX E-160

BindEX E-160 is a maleic anhydride modified linear low density polyethylene adhesive resin. It can be processed within different extrusion and co-extrusion technologies designed to process polyolefins. It is especially designed to combine aluminum sheets with polymer core in Aluminum composite panels, using extrusion coating process.

Properties

Physical Form: Masterbatch
Solid

Product families

Composite Materials — Additives

Functional Additives

Plastics — Masterbatches

Additive Masterbatches

Plastics — Polymer Additives

Surface Modifiers

Other characteristics

Brand: BindEX
Carrier: Linear Low Density Polyethylene (LLDPE), Resin-based; Linear Low Density Polyethylene (LLDPE); Resin-based
Functions: Adhesion Promoter, Coupling Agent
Processing Methods: Coextrusion, Extrusion
Compatible Polymers & Resins: Polyethylenes (PE)
Applications: Adhesion promoter between Polyethylene core and Aluminum sheets in Aluminum composite panels.. Can be used as coupling agent in polymer core to increase flame retardant loading in HFFR ACP panels.
Technology: Composite Materials
Plastics
Packaging Type: Bags
Super Sacks
Material Features: Non-Hygroscopic
Packaging Information: BindEX speciality polymers are supplied in pre-dried form in 25 Kg (55 lbs) PE lined, HD woven sack-laminated paper bags and 750 Kg (1650 lbs) FIBC's.. They should be stored in cool and dry place.
Processing Conditions: BindEX E-160 can be processed on most of the standard extrusion equipment designed to process conventional polyolefins.. Maximum processing temperature should not generally exceed 280°C.
Compatible Polymers and Resins: Polyethylenes (PE)
Composite Materials Functions: Adhesion Promoter
Coupling Agent
Plastics and Elastomers Functions: Adhesion Promoter
Coupling Agent
Storage and Handling Procedures: BindEX E-160 should be stored in a dry, cool, and well-ventilated area protected from UV-light.. Improper storage conditions may cause degradation and thus can adversely affect the physical properties of the product.
Plastics and Elastomers Processing Methods: Coextrusion
Extrusion

Technical data

Table 1 of 3

2 rows

Characteristic	Value	Unit	Method
Tensile Strength at Break	13	MPa	ASTM D638
Elongation at Break	700	%	ASTM D638

Table 2 of 3

5 rows

Characteristic	Value	Unit	Method
MFI (at 190°C/2.16 Kg)	3	g/10min	ASTM D1238
Density	0.923	g/cm³	ASTM D792
Bonded Maleic Anhydride	Low medium	—	PLUSS® method
Adhesion Strength	min. 6.0	Kg/25mm	PLUSS® method
Process Temperature	200 - 230	°C	PLUSS® method