BindEX E-188

BindEX E-188 is a maleic anhydride modified metallocene based linear low density polyethylene adhesive resin. It can be processed within different extrusion and co-extrusion technologies designed to process polyolefins. Due to its high MFI it has easy processability in cast film applications.

Properties

Physical Form: Masterbatch
Solid

Product families

Plastics — Masterbatches

Additive Masterbatches

Plastics — Polymer Additives

Surface Modifiers

Other characteristics

Brand: BindEX
Carrier: Metallocene Linear Low Density Polyethylene (mLLDPE)
Features: Easier Processing, Excellent Melt Flow, Non-Hygroscopic
Functions: Adhesion Promoter
Processing Methods: Cast Film Extrusion, Coextrusion, Extrusion, Film Extrusion
Compatible Polymers & Resins: High-Density Polyethylene (HDPE), Linear Low Density Polyethylene (LLDPE) , Low-Density Polyethylene (LDPE)
Applications: To adhere LLDPE or LDPE or HDPE and Nylon in multilayer cast films.; Its high MFI makes it suitable for cast application.; No dilution is required and should be used 100%.
Technology: Plastics
Packaging Type: Bags
Super Sacks
Material Features: Easier Processing
Excellent Melt Flow
Non-Hygroscopic
Packaging Information: BindEX speciality polymers are supplied in pre-dried form in 25 Kg (55 lbs) PE lined, HD woven sack-laminated paper bags and 750 Kg (1650 lbs) FIBC's.. They should be stored in cool and dry place.
Processing Conditions: BindEX E-188 can be processed on most of the standard extrusion equipments designed to process conventional polyolefins.. Maximum processing temperature should not generally exceed 270°C.
Compatible Polymers and Resins: High-Density Polyethylene (HDPE)
Linear Low Density Polyethylene (LLDPE)
Low-Density Polyethylene (LDPE)
Plastics and Elastomers End Uses: Cast Films
Film
Plastics and Elastomers Functions: Adhesion Promoter
Storage and Handling Procedures: BindEX E-188 should be stored in a dry, cool and well-ventilated area protected from UV-light.. Improper storage conditions may cause degradation and thus can adversely affect the physical properties of the product.
Plastics and Elastomers Processing Methods: Cast Film Extrusion
Coextrusion
Extrusion
Film Extrusion

Technical data

Table 1 of 4

2 rows

Characteristic	Value	Unit	Method
Tensile Strength at Break	16	MPa	ASTM D638/2010
Elongation at Break	700	%	ASTM D638/2010

Table 2 of 4

4 rows

Characteristic	Value	Unit	Method
MFI (at 190°C/2.16 Kg)	5	g/10min	ASTM D1238
Density	0.89	g/cm³	ASTM D792
Bonded Maleic Anhydride	Low	—	PLUSS® method
Yellowness Index	3	—	ASTM E-313

Table 3 of 4

1 row

Characteristic	Value	Unit	Method
Melting Temperature	114	°C	DSC