BindEX E-187
BindEX E-187 is a ready-to use tie resin to adhere barrier layer such as Nylon 6, Nylon 66 and EVOH with layers of PE or co-polymer of PP in a multilayer co-extruded structure made using blown film process. It is based on anhydride functionalized, Polyolefin. It is designed to be used as such, without dilution.
Product families
- Surface Modifiers
Other characteristics
- Brand
- BindEX
- Functions
- Adhesion Promoter
- Processing Methods
- Coextrusion, Extrusion
- Compatible Polymers & Resins
Ethylene Vinyl Alcohol (EVOH), Polyamide 6 (PA 6), Polyamide 66 (PA 66), Polyethylenes (PE), Polypropylenes (PP)
- Applications
Designed to use as a tie layer resin without dilution in conventional extrusion and co-extrusion equipment for making multilayer barrier films.. Can adhere to Nylon-6, Nylon 6,6, and EVOH
- Technology
- Plastics
- Packaging Type
- Bags
- Super Sacks
- Material Features
- Non-Hygroscopic
- Packaging Information
BindEX speciality polymers are supplied in pre-dried form in 25 Kg (55 lbs) PE lined, HD woven sack-laminated paper bags and 750 Kg (1650 lbs) FIBC's.. They should be stored in cool and dry place.
- Processing Conditions
BindEX E-187 can be processed on standard extrusion equipment designed to process conventional polyolefins.; Maximum processing temperature should not exceed 280°C.; At temperatures above 280°C, these speciality polymers can evolve low concentrations of fumes.; If overheated, more extensive decomposition may occur due to exposure of overheated polymers to atmospheric oxygen.; Adequate local ventilation should be provided to remove the fumes from the work area.
- Compatible Polymers and Resins
- Ethylene Vinyl Alcohol (EVOH)
- Polyamide 6 (PA 6)
- Polyamide 66 (PA 66)
- Polyethylenes (PE)
- Polypropylenes (PP)
- Plastics and Elastomers Functions
- Adhesion Promoter
- Storage and Handling Procedures
BindEX E-187 is mildly hygroscopic and should be stored in a dry, cool and well-ventilated area.; It is supplied in pre-dried moisture proof bags and thus does not need to be dried before processing.; In case of open bags, it is recommended that prior to processing, the requisite quantity of material should be dried in a hot air dryer or oven at 80-90°C for about 2 hours for obtaining best results.
- Plastics and Elastomers Processing Methods
- Coextrusion
- Extrusion
Technical data
Table 1 of 2
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| MFI (at 190°C/2.16 Kg) | 1.5 | g/10min | ASTM D1238 |
| Density | 0.91 | g/cm³ | ASTM D792 |
| Bonded Maleic Anhydride | Low | — | PLUSS® method |
| Yellowness Index | 1 | — | ASTM E-313 |
Table 2 of 2
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Melting Temperature | 117 | °C | DSC |