BindEX E-165

BindEX E-165 is a modified linear low density polyethylene adhesive resin designed for use in adhesive film for making Aluminum Composite Panels (ACP). The chemical modification provides excellent adhesion to both polyethylene and aluminum substrates. It is preferably used as outer layer in 3- layer coextruded blown film structure. It is this layer which faces aluminum sheet during lamination process. It can be processed on normal extruders used for processing of polyethylenes.

Properties

Physical Form: Masterbatch
Solid

Product families

Composite Materials — Additives

Functional Additives

Plastics — Masterbatches

Additive Masterbatches

Plastics — Polymer Additives

Surface Modifiers

Other characteristics

Brand: BindEX
Carrier: Linear Low Density Polyethylene (LLDPE), Resin-based; Linear Low Density Polyethylene (LLDPE); Resin-based
Functions: Coupling Agent
Processing Methods: Extrusion
Compatible Polymers & Resins: Polyethylenes (PE)
Applications: Adhesive layer in 3-layer film structure.; Coupling agent for HFFR polymer core in Aluminum composite panels.
Technology: Composite Materials
Plastics
Packaging Type: Bags
Super Sacks
Material Features: Easier Processing
Good Adhesion
Non-Hygroscopic
Packaging Information: BindEX speciality polymers are supplied in pre-dried form in 25 Kg (55 lbs) PE lined, HD woven sack-laminated paper bags and 500 Kg (1102 lbs) FIBC's.. They should be stored in cool and dry place.
Processing Conditions: BindEX E-165 can be processed on most standard extrusion equipment, designed to process conventional polyolefins.. Maximum processing temperature should not exceed 280°C.
Compatible Polymers and Resins: Polyethylenes (PE)
Composite Materials Functions: Coupling Agent
Plastics and Elastomers Functions: Coupling Agent
Storage and Handling Procedures: BindEX E-165 should be stored in a dry, cool and well-ventilated area protected from UV-light.. Improper storage conditions may cause degradation and thus can adversely affect the physical properties and performance of the product.
Plastics and Elastomers Processing Methods: Extrusion

Technical data

Table 1 of 3

2 rows

Characteristic	Value	Unit	Method
Tensile Strength at Break	15	MPa	ASTM D638
Elongation at Break	470	%	ASTM D638

Table 2 of 3

5 rows

Characteristic	Value	Unit	Method
MFI (at 190°C/2.16 Kg)	2	g/10min	ASTM D1238
Density	0.923	g/cm³	ASTM D792
Bonded Maleic Anhydride	Low medium	—	PLUSS® method
Adhesion Strength	6	Kg/25mm	PLUSS® method
Process Temperature	200 - 230	°C	PLUSS® method

Table 3 of 3