CarbonResin™ RPU 60

Chemical Family: Polyurethanes (PU)

CarbonResin™ RPU 60 is a tough, abrasion-resistant material that is a good choice for parts that require rigidity, strength, and durability. Rigid Polyurethane is our most versatile rigid material family. It is used across a wide range of industries, including consumer products, automotive, and industrial. RPU is comparable to ABS.

Properties

Physical Form: Liquid

Product families

Applications

Consumer Goods — Footwear

Automotive & Transportation — Automotive

Interior
Other Automotive Applications
Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Product Families

Plastics — 3D Printing Polymers

Photoactive Resins

Other characteristics

Brand: CarbonResin
Density: 1076.0 - 1076.0 kg/m³
End Uses: Automotive Applications, Automotive Interior Parts, Footwear, Safety Helmets
Polymer Name: Polyurethane (unspecified)
Processing Methods: 3D Printing, Digital Light Synthesis
Markets: Automotive & Transportation
Consumer Goods
Industrial
Technology: Plastics
Material Features: Abrasion Resistant
Durable
Good Rigidity
Good Strength
Good Surface Finish
Good Toughness
Country Availability: Canada
USA
Plastics and Elastomers End Uses: Automotive Applications
Automotive Interior Parts
Footwear
Safety Helmets
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: 3D Printing
Digital Light Synthesis

Technical data

Table 1 of 3

11 rows

Characteristic	Value	Unit	Method
Tensile Strength at Yield (Type V, 10 mm/min)	42 ± 2	MPa	ASTM D638
Ultimate Tensile Strength (Type V, 10 mm/min)	48 ± 8	MPa	ASTM D638
Tensile Modulus (Type V, 10 mm/min)	1600 ± 100	MPa	ASTM D638
Elongation at Break (Type V, 10 mm/min)	130 ± 10	%	ASTM D638
Elongation at Yield (Type V, 10 mm/min)	6 ± 1	%	ASTM D638
Flexural Strength	42 ± 2	MPa	ASTM D790
Flexural Modulus	1450 ± 500	MPa	ASTM D790
Charpy Notched Impact Strength	2.06 ± 0.11	kJ/m2	ISO 179-1/1eA
Izod Notched Impact Strength (Machined, 23°C)	29 ± 1	J/m	ASTM D256
Izod Notched Impact Strength (Machined, -30°C)	20 ± 4	J/m	ASTM D256
Izod Unnotched Impact Strength Impact Strength	933 ± 85	J/m	ASTM D4812

Table 2 of 3

3 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (-40, 40°C)	100	ppm/°C	ASTM E831
Heat Deflection Temperature (0.455 MPa, 66 psi)	58	°C	ASTM D648
Heat Deflection Temperature (1.82 MPa, 264 psi)	49	°C	ASTM D648

Table 3 of 3