CarbonResin™ RPU 61
- Chemical Family
- Polyurethanes (PU)
CarbonResin™ RPU 61 is a tough, and abrasion-resistant higher resolution material that is a good choice for parts that require rigidity, strength, and durability. Rigid Polyurethane is our most versatile rigid material family. It is used across a wide range of industries, including consumer products, automotive, and industrial. RPU is comparable to ABS.
Properties
- Physical Form
- Liquid
Product families
Applications
Applications
- Consumer Goods — Footwear
Automotive & Transportation — Automotive
- Interior
- Other Automotive Applications
- Powertrain & UTH
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
- Other Industrial Applications
Product Families
Plastics — 3D Printing Polymers
- Photoactive Resins
Other characteristics
- Brand
- CarbonResin
- Density
- 1074.0 - 1074.0 kg/m³
- End Uses
Automotive Applications, Automotive Interior Parts, Footwear, Grommets, Industrial Applications, Safety Helmets, Seals
- Polymer Name
- Polyurethane (unspecified)
- Processing Methods
- 3D Printing, Digital Light Synthesis
- Markets
- Automotive & Transportation
- Consumer Goods
- Industrial
- Technology
- Plastics
- Material Features
- Abrasion Resistant
- Durable
- Good Rigidity
- Good Strength
- Good Surface Finish
- Good Toughness
- Country Availability
- Canada
- USA
- Plastics and Elastomers End Uses
- Automotive Applications
- Automotive Interior Parts
- Footwear
- Grommets
- Industrial Applications
- Safety Helmets
- Seals
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- 3D Printing
- Digital Light Synthesis
Technical data
Table 1 of 3
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Strength at Yield (Type V, 10 mm/min) | 40 ± 2 | MPa | ASTM D638 |
| Ultimate Tensile Strength (Type V, 10 mm/min) | 42 ± 3 | MPa | ASTM D638 |
| Tensile Modulus (Type V, 10 mm/min) | 1500 ± 100 | MPa | ASTM D638 |
| Elongation at Break (Type V, 10 mm/min) | 120 ± 10 | % | ASTM D638 |
| Elongation at Yield (Type V, 10 mm/min) | 6 ± 1 | % | ASTM D638 |
| Flexural Strength | 37 ± 2 | MPa | ASTM D790 |
| Flexural Modulus | 1100 ± 100 | MPa | ASTM D790 |
| Charpy Notched Impact Strength | 2.31 ± 0.39 | kJ/m2 | ISO 179-1/1eA |
| Izod Notched Impact Strength (Machined, 23°C) | 27 ± 2 | J/m | ASTM D256 |
| Izod Notched Impact Strength (Machined, -30°C) | 22 ± 5 | J/m | ASTM D256 |
| Izod Unnotched Impact Strength Impact Strength | 1.2 ± 0.2 | kJ/m | ASTM D4812 |
Table 2 of 3
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (-40, 40°C) | 99 | ppm/°C | ASTM E831 |
Table 3 of 3
2 rows| Characteristic | Value | Method |
|---|---|---|
| Dielectric Constant (1 MHz) | 3.1 | ASTM D 150 |
| Dissipation Factor (1 MHz) | 0.017 | ASTM D 150 |