CarbonResin™ SIL 30
- Chemical Family
- Silicones
CarbonResin™ SIL 30 is a soft, biocompatible, and tear resistant silicone urethane elastomer that is ideal for comfortable skin-contact applications. SIL 30 is a silicone urethane. It is the first additive material to offer a unique combination of biocompatibility, low durometer, and tear-resistance. This material opens up the ability to print customized applications for comfortable skin contact products such as headphones, wristbands, and various attachments for wearables. SIL is a specialty material available for specific production applications.
Properties
- Physical Form
- Liquid
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics; Consumer Goods — Other Consumer Goods Applications
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Product Families
Plastics — 3D Printing Polymers
- Photoactive Resins
Other characteristics
- Brand
- CarbonResin
- Density
- 1070.0 - 1070.0 kg/m³
- End Uses
- Appliances, Consumer Applications
- Polymer Name
- Thermoplastic Silicone Vulcanizate (TPSiV)
- Processing Methods
- 3D Printing, Digital Light Synthesis
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Biocompatible
- Good Surface Finish
- Plastics and Elastomers End Uses
- Appliances
- Consumer Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- 3D Printing
- Digital Light Synthesis
Technical data
Table 1 of 4
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hardness | 35 (instant), 31 (5 sec) | Shore A | ASTM D2240 |
| Ultimate Tensile Strength (Die-C Shape, 500 mm/min) | 3.2 | MPa | ASTM D412 |
| Stress at 100 % Elongation (Die-C Shape, 500 mm/min) | 0.69 | MPa | ASTM D412 |
| Stress at 200 % Elongation (Die-C Shape, 500 mm/min) | 1.45 | MPa | ASTM D412 |
| Stress at 50 % Elongation (Die-C Shape, 500 mm/min) | 0.42 | MPa | ASTM D412 |
| Tear Strength (Die-C, die cut) | 9.6 | kN/m | ASTM D624 |
| Compression Set (23°C, 72 hrs) | 0.11 | — | ASTM D395-B |
| Bayshore Rebound Resilience | 0.2 | — | ASTM D2632 |
| Elongation at Break (Die-C Shape, 500 mm/min) | min. 330 | % | ASTM D412 |
Table 2 of 4
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density | 1.07 | g/cm3 | ISO 1183 |
| Density (liquid resin) | 1.05 | g/cm3 | ASTM D792 |
Table 3 of 4
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Glass Transition Temperature (DMA, tan (d)) | 8 | °C | ASTM D4065 |
Table 4 of 4
2 rows| Characteristic | Value | Method |
|---|---|---|
| Dissipation Factor (1 MHz) | 0.15 | ASTM D 150 |
| Dielectric Constant (1 MHz) | 7.6 | ASTM D150 |