ULTEM™ Resin 2110EPR
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
SABIC's Specialties Business 10% Glass fiber filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 and 5VA listing. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
Other characteristics
- Brand
- ULTEM™ Resin
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant, Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Printing & Packaging
- Availability
ULTEM™ resin is available in transparent and opaque custom colors, and can be glass filled for added stiffness.
- Flame Rating
- UL 94 5VA
- UL 94 V0
- Key Benefits
- Heat Resistance
- Dimensional Stability
- Dielectric Performance
- Miniaturization and Thin Wall
- Resilience
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Confirms to ECO-Label
- Low Toxicity
- No Added PFAS
Technical data
Table 1 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) | 119 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) | 119 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) | 3 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) | 3 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) | 5240 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) | 199 | MPa | ASTM D790 |
| Flexural Stress (Break, 2.6 mm/min, 100 mm span) | 193 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) | 4800 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) | 5170 | MPa | ASTM D790 |
Table 2 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.35 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) | 0.7 - 0.9 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) | 0.6 - 0.8 | % | SABIC method |
| Melt Flow Rate (at 337°C, 6.6 kgf) | 19 | g/10 min | ASTM D1238 |
Table 3 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) | 210 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) | 2.10E+02 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) | 210 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) | 205 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) | 212 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) | 207 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) | 0.000036 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) | 0.000081 | 1/°C | ASTM E831 |
| Relative Temperature Index (Electrical) ᵖ | 155 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ | 155 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ | 155 | °C | UL 746B |
Table 4 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| High Voltage Arc Track Rate (PLC) | 3 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) | 4 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 1) | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) | min. 0.75 | mm | UL 746A |
| Hot Wire Ignition (PLC 4) | min. 0.4 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 3) | min. 0.4 | mm | UL 746A |
| Arc Resistance (Tungsten, PLC) | 6 | PLC Code | ASTM D495 |
Table 5 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Instrumented Dart Impact Total Energy (at 23°C) | 10 | J | ASTM D3763 |
| Izod Impact (Unnotched, at 23°C) | 534 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) | 69 | J/m | ASTM D256 |
| Izod Impact (Reverse Notched, 3.2 mm) | 350 | J/m | ASTM D256 |
Table 6 of 7
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure | 0.3 - 0.7 | MPa |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | Hrs |
| Drying Time (Cumulative) | 24 | Hrs |
| Front - Zone 3 Temperature | 345 - 400 | °C |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 350 - 400 | °C |
| Middle - Zone 2 Temperature | 340 - 400 | °C |
| Mold Temperature | 135 - 165 | °C |
| Nozzle Temperature | 345 - 400 | °C |
| Rear - Zone 1 Temperature | 330 - 400 | °C |
| Screw Speed | 40 - 70 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.4 | mm | UL 94 |