LNP™ THERMOCOMP™ AM Compound AF004XXAR1

Chemical Family: Acrylonitrile Butadiene Styrene (ABS)

SABIC's Specialties Business LNP™ THERMOCOMP™ AM Compound AF004XXAR1 is a top-quality material based on acrylonitrile butadiene styrene (ABS) resin containing 20% glass fiber specifically designed for large format additive manufacturing (LFAM) applications. This grade is easy to process, has low warp, and provides excellent print surface quality, making it an ideal candidate for a broad range of applications and tooling, including thermoforming and vacuum forming. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts
Tooling & Moldmaking

Other characteristics

Brand: LNP™ THERMOCOMP™ AM Compound
Density: 1198.0 - 1198.0 kg/m³
Polymer Name: Acrylonitrile Butadiene Styrene (ABS)
Fillers Included: Glass Fiber
Processing Methods: 3D Printing, Large Format Additive Manufacturing (LFAM), Thermoforming
Note: ⁿ Tensile Stiffness (K) is a structural property defined as the stress/strain in the linear region of the stress/strain curve. Value depends on the geometry/shape and boundary/surrounding conditions.
Markets: Industrial
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Cost Effective
Easier Processing
Good Print Surface Quality
Good Printability
Good Processability
Low Warpage
No Added PFAS
Vacuum Forming
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: 3D Printing Applications
Industrial Applications
Industrial Parts
Tooling
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: 3D Printing
Large Format Additive Manufacturing (LFAM)
Thermoforming

Technical data

Table 1 of 4

8 rows

Characteristic	Value	Unit	Method
Tensile Stress (at 5mm/min, XZ Orientation)	63	MPa	ASTM D638 Modified
Tensile Stress (at 5mm/min, ZX Orientation)	21	MPa	ASTM D638 Modified
Tensile Strain (at 5mm/min, XZ Orientation)	1.8	%	ASTM D638 Modified
Tensile Strain (at 5mm/min, ZX Orientation)	1	%	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, XZ Orientation) ⁿ	5.1	GPa	ASTM D638 Modified
Tensile Stiffness (at 5mm/min, ZX Orientation)	2.6	GPa	ASTM D638 Modified
Flexural Stress (at 5mm/min, XZ Orientation)	35	MPa	ASTM D790 Modified
Flexural Stress (at 5mm/min, ZX Orientation)	91	MPa	ASTM D790 Modified

Table 2 of 4

1 row

Characteristic	Value	Method
Specific Gravity	1.198	ASTM D792

Table 3 of 4