LNP™ LUBRICOMP™ Compound JD4901
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
LNP LUBRICOMP JD4901 compound is based on Polyetherimide (PEI) resin containing 20% glass fiber, 10% PTFE. Added features of this grade include: Wear Resistant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Semiconductor Manufacturing
- Switches & Relays
- Terminal Blocks Plugs & Sockets
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 6470.0 - 6470.0 MPa
- Additives Included
- Lubricant (PTFE)
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Material Features
- Friction Resistant
- High Temperature Resistance
- Very Good Heat Resistance
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Amusement Machine
- Appliances
- Building Materials
- Burn-In Socket
- Cell Phones
- Circuit Protection
- Commercial Appliance
- Computer Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield) ¹¹ | 125 | MPa | SABIC - Japan Method |
| Tensile Strain (Break) ¹¹ | 3 | % | SABIC - Japan Method |
| Flexural Stress ¹¹ | 190 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 6470 | MPa | ASTM D790 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.48 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.18 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.2 - 0.3 | % | SABIC method |
Table 3 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 213 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 105 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 105 | °C | UL 746B |
Table 4 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Surface Resistivity ¹¹ | 1.00E+16 | Ω | ASTM D257 |
Table 5 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 78 | J/m | ASTM D256 |
Table 6 of 7
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure (Plastic Pressure) ⁷ | 5 - 10 | MPa |
| Drying Temperature ⁷ | 150 | °C |
| Drying Time ⁷ | 4 - 6 | Hrs |
| Front - Zone 3 Temperature ⁷ | 380 - 410 | °C |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 380 - 410 | °C |
| Middle - Zone 2 Temperature ⁷ | 370 - 400 | °C |
| Mold Temperature ⁷ | 140 - 170 | °C |
| Nozzle Temperature ⁷ | 380 - 405 | °C |
| Rear - Zone 1 Temperature ⁷ | 360 - 390 | °C |
| Screw Speed (Circumferential speed) ⁷ | 0.1 - 0.2 | m/s |
| Shot to Cylinder Size ⁷ | 40 - 70 | % |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |