ULTEM™ Resin 1110F
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
SABIC's Specialties Business Enhanced flow Polyetherimide (Tg 217C). ECO Conforming. US FDA and EU Food Contact compliant, NSF 51 listing. UL94 V0 and 5VA listing. Effective June 2007, this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU1110. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Other characteristics
- Brand
- ULTEM™ Resin
- Polymer Name
- Polyether Imide (PEI)
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Note
ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.. ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Personal Care
- Printing & Packaging
- Availability
ULTEM™ resin is available in transparent and opaque custom colors, and can be glass filled for added stiffness.
- Flame Rating
- UL 94 5VA
- UL 94 V0
- UL 94 V2
- Key Benefits
- Heat Resistance
- Dimensional Stability
- Dielectric Performance
- Miniaturization and Thin Wall
- Resilience
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Confirms to ECO-Label
- Food Contact Acceptable
- Low Toxicity
- No Added PFAS
Technical data
Table 1 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Taber Abrasion (CS-17, 1 kg) | 10 | mg/1000cy | SABIC method |
| Tensile Stress (Yield, Type I, 5 mm/min) | 110 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) | 70 | % | ASTM D638 |
| Tensile Stress (Yield, 50 mm/min) | 110 | MPa | ISO 527 |
| Tensile Modulus (at 5 mm/min) | 3720 | MPa | ASTM D638 |
| Tensile Stress (Break, 50 mm/min) | 80 | MPa | ISO 527 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) | 165 | MPa | ASTM D790 |
| Tensile Strain (Yield, 50 mm/min) | 6 | % | ISO 527 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) | 3720 | MPa | ASTM D790 |
| Tensile Strain (Break, 50 mm/min) | 10 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) | 3500 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) | 140 | MPa | ISO 178 |
Table 2 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow, 3.2 mm) | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 337°C, 6.6 kgf) | 16 | g/10 min | ASTM D1238 |
| Specific Gravity | 1.36 | — | ASTM D792 |
| Mold Shrinkage (on Tensile Bar, flow) | 0.5 - 0.7 | % | SABIC method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) | 1.2 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) | 0.65 | % | ISO 62 |
| Melt Volume Rate (at 340°C, 5.0 kg) | 12 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 360°C, 5.0 kg) | 21 | cm³/10 min | ISO 1133 |
Table 3 of 7
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) | 198 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ | 170 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ | 170 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ | 170 | °C | UL 746B |
| Thermal Conductivity | 0.26 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at 23°C to 150°C, flow) | 0.00005 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 150°C, xflow) | 0.00005 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (at 123°C to 127°C) | Pass | — | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate A/50) | 210 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) | 200 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) | 205 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) | 200 | °C | ISO 75/Be |
Table 4 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| High Voltage Arc Track Rate (PLC) | 2 | PLC Code | UL 746A |
| Arc Resistance (Tungsten, PLC) | 5 | PLC Code | ASTM D495 |
| Comparative Tracking Index (UL, PLC) | 4 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 1) | min. 3 | mm | UL 746A |
| Hot Wire Ignition (PLC 2) | min. 0.75 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 3) | min. 3 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 4) | min. 0.75 | mm | UL 746A |
| Volume Resistivity | 1.00E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity (ROA) | min. 1.E+15 | Ω | IEC 60093 |
| Dielectric Strength (in oil, at 3.2mm) | 17.2 | kV/mm | IEC 60243-1 |
| Dissipation Factor (at 50/60 Hz) | 0.0016 | — | IEC 60250 |
| Comparative Tracking Index ʳ | 175 | V | IEC 60112 |
Table 5 of 7
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Reverse Notched, 3.2 mm) | 1922 | J/m | ASTM D256 |
| Color (at 23°C) | 23 | J | ASTM D3029 |
| Izod Impact (Notched, 80*10*4, at 23°C) | 4 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) | 4 | kJ/m² | ISO 180/1A |
Table 6 of 7
21 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure | 0.3 - 0.7 | MPa |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | Hrs |
| Drying Time (Cumulative) | 24 | Hrs |
| Front - Zone 3 Temperature | 345 - 400 | °C |
| Front - Zone 3 Temperature | 370 - 410 | °C |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 350 - 400 | °C |
| Melt Temperature | 360 - 400 | °C |
| Middle - Zone 2 Temperature | 340 - 400 | °C |
| Middle - Zone 2 Temperature | 360 - 400 | °C |
| Mold Temperature | 135 - 165 | °C |
Table 7 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VA Flame Class Rating) ᵖ | min. 3 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |
| UL Recognized (94V-2 Flame Class Rating) ᵖ | min. 0.4 | mm | UL 94 |
| Glow Wire Flammability Index (passes at 960°C) ʳ ᵖ | 3.2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) ᵖ | 47 | % | ISO 4589 |