LNP™ COLORCOMP™ Compound D10008PR
- Chemical Family
- Polycarbonate (PC)
LNP COLORCOMP D10008PR compound is based on Polycarbonate (PC) resin. Added features of this grade include: Flame Retardant, Exceptional Processing, Mold Release.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Housewares
- Consumer Goods — Sports & Recreation
- Interior
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
Product Families
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LNP™ COLORCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Additives Included
- Flame Retardant, Mold Release Agent
- Flame Retardant
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Custom
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 V2
- Technology
- Plastics
- Material Features
- Excellent Aesthetics
- Flame Retardant
- Good Aesthetics
- Good Mold Release
- Good Processability
- Good Surface Appearance
- High Flowability
- Non-brominated
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Interior Parts
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 8
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 65 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 120 | % | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 93 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2300 | MPa | ASTM D790 |
Table 2 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.2 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 25 | g/10 min | ASTM D1238 |
Table 3 of 8
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 126 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 130 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Table 4 of 8
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hot Wire Ignition (PLC) ¹¹ | 2 | PLC Code | UL 746A |
| High Voltage Arc Track Rate (PLC) ¹¹ | 2 | PLC Code | UL 746A |
| High Ampere Arc Ignition (Surface, PLC) ¹¹ | 1 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
| Hot Wire Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 3) ¹¹ | min. 1.1 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 1) ¹¹ | min. 3 | mm | UL 746A |
| High Ampere Arc Ignition (PLC 2) ¹¹ | min. 1.5 | mm | UL 746A |
Table 5 of 8
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Light Transmission (at 2.54 mm) ¹¹ | 88 | % | ASTM D1003 |
| Haze (at 2.54 mm) ¹¹ | 1 | % | ASTM D1003 |
Table 6 of 8
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 640 | J/m | ASTM D256 |
| Tensile Impact Strength (Type S) ¹¹ | 378 | kJ/m² | ASTM D1822 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 54 | J | ASTM D3763 |
Table 7 of 8
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 3 - 4 | Hrs |
| Drying Time (Cumulative) ⁷ | 48 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 270 - 295 | °C |
| Nozzle Temperature ⁷ | 265 - 290 | °C |
| Front - Zone 3 Temperature ⁷ | 270 - 295 | °C |
| Middle - Zone 2 Temperature ⁷ | 260 - 280 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 270 | °C |
| Mold Temperature ⁷ | 70 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 8 of 8
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94V-2 Flame Class Rating) ᵖ | min. 1.1 | mm | UL 94 |