LNP™ LUBRICOMP™ Compound YL003C
- Chemical Family
- Polyesters
SABIC's Specialties Business LNP LUBRICOMP YL003C compound is based on Polyester Elastomer resin containing 15% PTFE. Added features of this grade include: LNP Clean Compounding Technology, Wear Resistant.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Equipment & Parts
- Consumer Electronics
- Displays
- Industrial Automation
- Connectors
- Semiconductor Manufacturing
- Switches & Relays
Product Families
- Thermoplastic Polyester Elastomers (TPE-E)
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Density
- 1270.0 - 1270.0 kg/m³
- End Uses
Cell Phones, Computer Components, Displays, Electrical Components, Electrical/Electronic Applications, Industrial Applications, Semiconductor Applications, Tablets
- Polymer Name
- Thermoplastic Polyester Elastomer
- Strain at Break
- 90.0 - 90.0 %
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- Markets
- Consumer Goods
- Electrical & Electronics
- Industrial
- Flame Rating
- UL 94 HB
- Technology
- Elastomers
- Fillers Included
- PTFE
- Additives Included
- Heat Stabilizer
- Lubricant (PTFE)
- Mold Release Agent
- Material Features
- Friction Resistant
- Good Mold Release
- Heat Stabilized
- Low Liquid Particle Count
- Low Outgassing
- Unreinforced
- Wear Resistant
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Cell Phones
- Computer Components
- Displays
- Electrical Components
- Electrical/Electronic Applications
- Industrial Applications
- Semiconductor Applications
- Tablets
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 22 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 90 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 280 | MPa | ASTM D638 |
| Flexural Stress ¹¹ | 19 | MPa | ASTM D790 |
| Flexural Stress ¹¹ | 12 | MPa | ISO 178 |
| Flexural Modulus ¹¹ | 290 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 280 | MPa | ISO 178 |
| Hardness (Shore D) ¹¹ | 56 | — | ASTM D2240 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | min. 450 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 260 | MPa | ISO 527 |
Table 2 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.27 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.27 | g/cm³ | ASTM D792 |
| Water Absorption (at 23°C, 48hrs) ¹¹ | 0.2 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.5 - 1.7 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 1.6 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.7 - 1.9 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1.8 | % | ISO 294 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.5 | % | ISO 62-1 |
Table 3 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 85 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 54 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00011 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00011 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00018 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00018 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 88 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 57 | °C | ISO 75/Af |
Table 4 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 580 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 150 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*3, at 23°C) ¹¹ | 48 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 23 | kJ/m² | ISO 180/1U |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.1 | % |
| Melt Temperature ⁷ | 215 - 240 | °C |
| Front - Zone 3 Temperature ⁷ | 225 - 240 | °C |
| Middle - Zone 2 Temperature ⁷ | 205 - 215 | °C |
| Rear - Zone 1 Temperature ⁷ | 180 - 195 | °C |
| Mold Temperature ⁷ | 25 - 55 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | 1 | mm | UL 94 |