LNP™ THERMOCOMP™ Compound DC0041PR

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP™ THERMOCOMP™ DC0041PR compound is based on Polycarbonate (PC) resin containing 20% carbon fiber. Added features of this grade include: Electrically Conductive, Non-Brominated, Non-Chlorinated Flame Retardant, PCR content up to 30%.

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Density: 1320.0 - 1320.0 kg/m³
Polymer Name: Polycarbonate (PC)
Labeling Claims: Bromine-free, Chlorine-free, Contains PCR Resin, Recyclable, Recycled, Sustainable; Bromine-free; Chlorine-free; Contains PCR Resin; Recyclable; Recycled; Sustainable
Fillers Included: Carbon Fiber, Talc
Carbon Fiber
Talc
Additives Included: Flame Retardant, Heat Stabilizer, Mold Release Agent; Flame Retardant; Heat Stabilizer; Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 V0
Technology: Plastics
Material Features: Cost Effective
Electrically Conductive
Flame Retardant
Good Mold Release
Heat Stabilized
High Ductility
High Impact Resistance
High Stiffness
Country Availability: Canada
China (Mainland)
Mexico
USA

Technical data

Table 1 of 6

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	160	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.1	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	19000	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	200	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	17500	MPa	ASTM D790

Table 2 of 6

3 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.32	—	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.08	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.33	%	ASTM D955

Table 3 of 6

4 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	86	°C	ASTM D648
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Table 4 of 6

3 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	400	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	55	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	9	J	ASTM D3763

Table 5 of 6

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	70	°C
Drying Time ⁷	4	Hrs
Maximum Moisture Content ⁷	0.05	%
Melt Temperature ⁷	275 - 310	°C
Front - Zone 3 Temperature ⁷	280 - 300	°C
Middle - Zone 2 Temperature ⁷	270 - 290	°C
Rear - Zone 1 Temperature ⁷	260 - 280	°C
Mold Temperature ⁷	60 - 80	°C
Back Pressure ⁷	0.2 - 0.3	MPa
Screw Speed ⁷	30 - 63	rpm

Table 6 of 6

1 row

Characteristic	Value	Unit	Method
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 0.8	mm	UL 94