LNP™ THERMOCOMP™ Compound UF007SXC

Chemical Family: Polyamides

SABIC's Specialties Business LNP THERMOCOMP UF007SXC compound is based on Polyphthalamide (PPA) resin containing 35% glass fiber. Added features of this grade include: Heat Stabilized. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Semiconductor Manufacturing
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyphthalamide (PPA)
Fillers Included: Glass Fiber
Flexural Modulus: 9100.0 - 9100.0 MPa
Additives Included: Heat Stabilizer
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Industrial
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Cost Effective
Heat Stabilized
High Stiffness
High Temperature Resistance
No Added PFAS
Very Good Heat Resistance
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Under The Hood
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, 5 mm/min) ¹¹	204	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.3	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	11000	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	280	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	9100	MPa	ISO 178

Table 2 of 5

2 rows

Characteristic	Value	Unit	Method
Mold Shrinkage (flow) ᵍ ¹¹	0.18	%	SABIC method
Density ¹¹	1.44	g/cm³	ISO 1183

Table 3 of 5

3 rows

Characteristic	Value	Unit	Method
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000024	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000058	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	258	°C	ISO 75/Af

Table 4 of 5