LNP™ THERMOCOMP™ Compound WF006H

Chemical Family: Polyesters

SABIC's Specialties Business LNP THERMOCOMP WF006H compound is based on Polybutylene Terephthalate (PBT) resin containing 30% glass fiber. Added features of this grade include: Healthcare. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Healthcare & Pharma — Medical

Medical Devices & Assemblies
Surgical Instruments & Trays

Printing & Packaging — Packaging

Healthcare Packaging
Industrial & Transport Packaging

Electrical & Electronics — Parts & Components

Housings & Enclosures

Product Families

Plastics — Engineering & Specialty Polymers

Polyesters & Copolyesters

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polybutylene Terephthalate (PBT)
Fillers Included: Glass Fiber
Flexural Modulus: 9440.0 - 9440.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Electrical & Electronics
Healthcare & Pharma
Printing & Packaging
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Cost Effective
Good Mold Release
High Modulus
High Stiffness
No Added PFAS
Country Availability: Canada
China (Mainland)
Mexico
USA
Plastics and Elastomers End Uses: Electrical Enclosure
Electrical Internal Frame
Internal Armature
Medical Devices
Medical Packaging
Medical/Healthcare Applications
Pharmaceutical Packaging
Surgical Devices
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	119	MPa	ASTM D638
Tensile Strain (Break) ¹¹	2.7	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	10440	MPa	ASTM D638
Flexural Stress ¹¹	186	MPa	ASTM D790
Flexural Modulus ¹¹	9440	MPa	ASTM D790

Table 2 of 5

2 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.62	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.6	%	ASTM D955

Table 3 of 5

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	208	°C	ASTM D648