LNP™ THERMOCOMP™ Compound PF00C
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP THERMOCOMP PF00C compound is based on Nylon 6 resin containing 60% glass fiber. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyamide 6 (PA 6)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 19380.0 - 19380.0 MPa
- Additives Included
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Good Mold Release
- High Modulus
- High Stiffness
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 2.10E+02 | MPa | ASTM D638 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 206 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 3 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 2.4 | % | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 20400 | MPa | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 22380 | MPa | ASTM D638 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 312 | MPa | ISO 178 |
| Flexural Stress ¹¹ | 365 | MPa | ASTM D790 |
| Flexural Modulus ¹¹ | 19380 | MPa | ASTM D790 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 307 | MPa | ISO 178 |
| Flexural Strain (Break, at 2 mm/min) ¹¹ | 3.7 | % | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 16700 | MPa | ISO 178 |
Table 2 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.72 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.71 | g/cm³ | ASTM D792 |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.3 | % | SABIC method |
Table 3 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 210 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000017 | 1/°C | ISO 11359-2 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000065 | 1/°C | ISO 11359-2 |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 219 | °C | ISO 75/Bf |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 206 | °C | ISO 75/Af |
Table 4 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1229 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 170 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 90 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 13 | kJ/m² | ISO 180/1A |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 - 0.25 | % |
| Melt Temperature ⁷ | 265 - 275 | °C |
| Front - Zone 3 Temperature ⁷ | 275 - 290 | °C |
| Middle - Zone 2 Temperature ⁷ | 265 - 275 | °C |
| Rear - Zone 1 Temperature ⁷ | 250 - 260 | °C |
| Mold Temperature ⁷ | 80 - 95 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | 1.5 | mm | UL 94 |