LNP™ COLORCOMP™ Compound D1000E

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP COLORCOMP D1000E compound is based on unfilled Polycarbonate (PC) resin. Added features of this grade include: Easy Molding. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Housewares
Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 HB
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Easy To Mold
Excellent Aesthetics
Good Aesthetics
Good Moldability
Good Processability
Good Surface Appearance
No Added PFAS
Non-Halogenated
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Interior Parts
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Containers
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 8

9 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	62	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	68	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	7	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	130	%	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	96	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2340	MPa	ASTM D790
Hardness (Rockwell M) ¹¹	70	—	ASTM D785
Hardness (Rockwell R) ¹¹	118	—	ASTM D785
Taber Abrasion (CS-17, 1 kg) ¹¹	1.00E+01	mg/1000cy	ASTM D1044

Table 2 of 8

8 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.2	—	ASTM D792
Specific Volume ¹¹	0.83	cm³/g	ASTM D792
Density ¹¹	1.19	g/cm³	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.15	%	ASTM D570
Water Absorption (at 23°C, saturated) ¹¹	0.35	%	ASTM D570
Water Absorption (Equilibrium, at 100°C) ¹¹	0.58	%	ASTM D570
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.5 - 0.7	%	SABIC method
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	10.5	g/10 min	ASTM D1238

Table 3 of 8

9 rows

Characteristic	Value	Unit	Method
Vicat Softening Temperature (Rate B/50) ¹¹	154	°C	ASTM D1525
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹	137	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	132	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹	0.0000684	1/°C	ASTM E831
Specific Heat ¹¹	1.25	J/g-°C	ASTM C351
Thermal Conductivity ¹¹	0.27	W/m-°C	ASTM C177
Relative Temperature Index (Electrical) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	130	°C	UL 746B

Table 4 of 8

13 rows

Characteristic	Value	Unit	Method
Volume Resistivity ¹¹	1.00E+17	Ω.cm	ASTM D257
Dielectric Strength (in air, at 3.2mm) ¹¹	14.9	kV/mm	ASTM D149
Relative Permittivity (50/60 Hz) ¹¹	3.17	—	ASTM D150
Relative Permittivity (1 MHz) ¹¹	2.96	—	ASTM D150
Dissipation Factor (at 50/60 Hz) ¹¹	0.0009	—	ASTM D150
Dissipation Factor (at at 1 MHz) ¹¹	0.01	—	ASTM D150
High Voltage Arc Track Rate (PLC) ¹¹	4	PLC Code	UL 746A
Comparative Tracking Index (UL, PLC) ¹¹	2	PLC Code	UL 746A
Hot Wire Ignition (PLC 2) ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 3) ¹¹	min. 1.1	mm	UL 746A
High Ampere Arc Ignition (PLC 0) ¹¹	min. 1.5	mm	UL 746A
High Ampere Arc Ignition (PLC 1) ¹¹	min. 3	mm	UL 746A

Table 5 of 8

3 rows

Characteristic	Value	Unit	Method
Light Transmission (at 2.54 mm) ¹¹	88	%	ASTM D1003
Haze (at 2.54 mm) ¹¹	1	%	ASTM D1003
Refractive Index ¹¹	1.586	—	ASTM D542

Table 6 of 8

5 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	3204	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	801	J/m	ASTM D256
Tensile Impact Strength (Type S) ¹¹	577	kJ/m²	ASTM D1822
Falling Dart Impact (at 23°C) ¹¹	169	J	ASTM D3029
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	63	J	ASTM D3763

Table 7 of 8

14 rows

Characteristic	Value	Unit
Drying Temperature ⁷	120	°C
Drying Time ⁷	3 - 4	Hrs
Drying Time (Cumulative) ⁷	48	Hrs
Maximum Moisture Content ⁷	0.02	%
Melt Temperature ⁷	295 - 315	°C
Nozzle Temperature ⁷	290 - 310	°C
Front - Zone 3 Temperature ⁷	295 - 315	°C
Middle - Zone 2 Temperature ⁷	280 - 305	°C
Rear - Zone 1 Temperature ⁷	270 - 295	°C
Mold Temperature ⁷	70 - 95	°C
Back Pressure ⁷	0.3 - 0.7	MPa
Screw Speed ⁷	40 - 70	rpm

Table 8 of 8