LNP™ COLORCOMP™ Compound D1000FL

Chemical Family: Polycarbonate (PC)

LNP COLORCOMP D1000FL compound is based on unfilled Polycarbonate (PC) resin. Added features of this grade include: Superior Molding, Low Extractable.

Product families

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Materials

Pipes & Plumbing

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Printing & Packaging — Packaging

Food & Beverage Packaging
Industrial & Transport Packaging
Non-Food Consumer Packaging

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polycarbonate (PC)
Additives Included: Mold Release Agent
Processing Methods: Injection Molding
Note: ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Markets: Building & Construction
Consumer Goods
Electrical & Electronics
Printing & Packaging
Flame Rating: UL 94 HB
UL 94 V2
Technology: Plastics
Labeling Claims: Food Contact Acceptable
Material Features: Excellent Aesthetics
Food Contact Acceptable
Good Aesthetics
Good Mold Release
Good Moldability
Good Surface Appearance
High Durability
High Flowability
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Building Materials
Consumer Applications
Food Containers
Food Packaging
Home Appliances
Hoses
Pipes
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

3 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	64	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	6	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2390	MPa	ASTM D638

Table 2 of 6

2 rows

Characteristic	Value	Unit	Method
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.3	%	ASTM D570
Density ¹¹	1.2	g/cm³	ISO 1183

Table 3 of 6

5 rows

Characteristic	Value	Unit	Method
Thermal Conductivity ¹¹	0.17	W/m-°C	ASTM E1530
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	125	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	125	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	115	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	125	°C	UL 746B

Table 4 of 6

7 rows

Characteristic	Value	Unit	Method
Comparative Tracking Index (UL, PLC) ¹¹	0	PLC Code	UL 746A
Hot Wire Ignition (PLC 1) ¹¹	min. 6	mm	UL 746A
Hot Wire Ignition (PLC 2) ¹¹	min. 1.5	mm	UL 746A
High Ampere Arc Ignition (PLC 1) ¹¹	min. 3	mm	UL 746A
High Ampere Arc Ignition (PLC 2) ¹¹	min. 1.5	mm	UL 746A
High Voltage Arc Track Rate (PLC) ¹¹	0	PLC Code	UL 746A
Arc Resistance (Tungsten, PLC) ¹¹	7	PLC Code	ASTM D495

Table 5 of 6

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	120	°C
Drying Time ⁷	4	Hrs
Maximum Moisture Content ⁷	0.02	%
Melt Temperature ⁷	305 - 325	°C
Front - Zone 3 Temperature ⁷	320 - 330	°C
Middle - Zone 2 Temperature ⁷	310 - 320	°C
Rear - Zone 1 Temperature ⁷	295 - 305	°C
Mold Temperature ⁷	80 - 110	°C
Back Pressure ⁷	0.2 - 0.3	MPa
Screw Speed ⁷	30 - 60	rpm

Table 6 of 6