LNP™ THERMOCOMP™ Compound UF0069S

Chemical Family: Polyamides

LNP THERMOCOMP UF0069S compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber. Added features of this grade include: Flame Retardant, Heat Stabilized.

Product families

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics
Displays

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Semiconductor Manufacturing
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyphthalamide (PPA)
Fillers Included: Glass Fiber
Additives Included: Flame Retardant, Heat Stabilizer
Flame Retardant
Heat Stabilizer
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Industrial
Flame Rating: UL 94 5VA
UL 94 V0
Technology: Plastics
Material Features: Cost Effective
Flame Retardant
Heat Stabilized
High Stiffness
High Temperature Resistance
Very Good Heat Resistance
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Under The Hood
Cell Phones
Commercial Appliance
Computer Components
Consumer Applications
Displays
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹¹	166	MPa	ISO 527
Tensile Stress (Break) ¹¹	181	MPa	ASTM D638
Tensile Strain (Break) ¹¹	1.9	%	ASTM D638
Tensile Strain (Break) ¹¹	1.7	%	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	13780	MPa	ASTM D638
Flexural Stress ¹¹	264	MPa	ISO 178
Flexural Stress ¹¹	258	MPa	ASTM D790
Flexural Modulus ¹¹	12060	MPa	ASTM D790
Flexural Modulus ¹¹	12320	MPa	ISO 178
Tensile Modulus (at 1 mm/min) ¹¹	12070	MPa	ISO 527

Table 2 of 6

8 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.65	g/cm³	ISO 1183
Density ¹¹	1.655	g/cm³	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.24	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.22	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.6	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.59	%	ISO 294
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.26	%	ISO 62

Table 3 of 6

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed)	250	°C	ASTM D648

Table 4 of 6

5 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	550	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	90	J/m	ASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	2	J	ASTM D3763
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	44	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	9	kJ/m²	ISO 180/1A

Table 5 of 6