SABIC's Specialties BusinessLNP™ THERMOCOMP™ Compound WX93111
SABIC's Specialties Business LNP THERMOCOMP WX93111 compound is based on Polybutylene Terephthalate (PBT) resin containing 20% glass fiber. Added features of this grade include: : Improved CTI, Flame Retardant. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Brand:
- LNP™ THERMOCOMP™ Compound
Polymer Name:
- Polybutylene Terephthalate (PBT)
Fillers Included:
- Glass Fiber
Flexural Modulus:
- 8900.0 - 8900.0 MPa
Additives Included:
- Flame Retardant
Processing Methods:
- Injection Molding
Note:
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets:
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
Technology:
- Plastics
Chemical Family:
- Polyesters
Labeling Claims:
- No Added PFAS
Material Features:
- Cost Effective
- Flame Retardant
- High Modulus
- High Stiffness
- No Added PFAS
Country Availability:
- Canada
- China (Mainland)
- Mexico
- USA
Plastics and Elastomers End Uses:
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Containers
- Displays
- Electrical Components
- Electrical Enclosure
- Electrical Internal Frame
- Electrical/Electronic Applications
- Food Preparation Equipment
- Garden Equipment
- Home Appliances
- Internal Armature
- Lawn Equipment
- Personal Accessories
- Pool Covers
- Sporting Goods
- Tablets
- Tarpaulins
- Turf Applications
Plastics and Elastomers Functions:
- Resin
Plastics and Elastomers Processing Methods:
- Injection Molding
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
Building & Construction — Decorative Materials & Finishes
- Artificial Turf
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- Polyesters & Copolyesters
| Characteristic name | Value | Unit of measurement | Test method |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 43 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 0.6 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8900 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 244 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 8900 | MPa | ISO 178 |
| Characteristic name | Value | Unit of measurement | Test method |
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.3 | % | SABIC method |
| Density ¹¹ | 1.8 | g/cm³ | ISO 1183 |
| Characteristic name | Value | Unit of measurement | Test method |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000034 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000077 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 135 | °C | ISO 75/Af |
| Characteristic name | Value | Unit of measurement | Test method |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 5 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
| Characteristic name | Value | Unit of measurement | Test method |
| Drying Temperature ⁷ | 120 | °C | - |
| Drying Time ⁷ | 4 | Hrs | - |
| Maximum Moisture Content ⁷ | 0.05 | % | - |
| Melt Temperature ⁷ | 245 - 260 | °C | - |
| Front - Zone 3 Temperature ⁷ | 250 - 260 | °C | - |
| Middle - Zone 2 Temperature ⁷ | 245 - 255 | °C | - |
| Rear - Zone 1 Temperature ⁷ | 230 - 245 | °C | - |
| Mold Temperature ⁷ | 80 - 100 | °C | - |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa | - |
| Screw Speed ⁷ | 30 - 60 | rpm | - |