LNP™ THERMOCOMP™ Compound JF002R
- Chemical Family
- Polysulfones
LNP THERMOCOMP JF002R compound is based on Polyethersulfone (PES) resin containing 10% glass fiber/glass bead. Added features of this grade include: Mold Release.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- High Performance Thermoplastics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyethersulfone (PES)
- Fillers Included
Glass Bead, Glass Bead/Glass Fiber, Glass Fiber, PTFE; Glass Bead; Glass Bead/Glass Fiber; Glass Fiber; PTFE
- Flexural Modulus
- 3200.0 - 3200.0 MPa
- Additives Included
- Flame Retardant, Mold Release Agent
- Flame Retardant
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые размеры литья, литье крупных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Cost Effective
- Flame Retardant
- Good Mold Release
- High Modulus
- High Stiffness
- High Temperature Resistance
- Very Good Heat Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Consumer Applications
- Containers
- Displays
- Doors
- Electrical Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 83 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 4.5 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 3500 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 133 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 3.20E+03 | MPa | ISO 178 |
Table 2 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.45 | g/cm³ | ISO 1183 |
Table 3 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000043 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000055 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 221 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 212 | °C | ISO 75/Af |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 45 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Front - Zone 3 Temperature ⁷ | 370 - 380 | °C |
| Maximum Moisture Content ⁷ | 0.05 | % |
| Melt Temperature ⁷ | 355 - 370 | °C |
| Middle - Zone 2 Temperature ⁷ | 360 - 370 | °C |
| Mold Temperature ⁷ | 140 - 150 | °C |
| Rear - Zone 1 Temperature ⁷ | 345 - 355 | °C |
| Screw Speed ⁷ | 60 - 100 | rpm |