LNP™ THERMOCOMP™ Compound OF00AN

Chemical Family: Polyphenylene Sulfide (PPS)

SABIC's Specialties Business LNP THERMOCOMP OF00AN compound is based Polyphenylene Sulfide (PPS) containing 50% glass fiber. Added features include: High Modulus, Impact Modified, Low Chloride content, Good Warpage Control, Inherently Flame Retardant. Excellent High Heat and Chemical Resistance and Good Metal Bonding Strength suitable for Nano-Molding Technology (NMT) applications. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Electrical & Electronics — Devices & Assemblies

Industrial Automation

Electrical & Electronics — Parts & Components

Connectors
Housings & Enclosures
Switches & Relays

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Other characteristics

Brand: LNP™ THERMOCOMP™ Compound
Polymer Name: Polyphenylene Sulfide (PPS)
Fillers Included: Glass Fiber
Flexural Modulus: 15400.0 - 15400.0 MPa
Additives Included: Flame Retardant
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Electrical & Electronics
Flame Rating: UL 94 V0
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Cost Effective
Dimensional Stability
Flame Retardant
Good Adhesion
High Linearity
High Modulus
High Stiffness
Low Warpage
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Electrical Components
Electrical Enclosure
Electrical Internal Frame
Electrical/Electronic Applications
Internal Armature
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 7

10 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	203	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.8	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	16700	MPa	ASTM D638
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	285	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	15200	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	205	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.8	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	16800	MPa	ISO 527
Flexural Strength (at 2 mm/min) ¹¹	290	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	15400	MPa	ISO 178

Table 2 of 7

9 rows

Characteristic	Value	Unit	Method
Density ¹¹	1.7	g/cm³	ASTM D792
Melt Flow Rate (at 315°C, 5.0 kgf) ¹¹	30	g/10 min	ASTM D1238
Melt Volume Rate (at 315°C, 5.0 kg) ¹¹	18	cm³/10 min	ISO 1133
Specific Gravity ¹¹	1.7	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.01	%	ISO 62-4
Water Absorption (at 23°C, 24hrs) ¹¹	0.02	%	ISO 62-1
Water Absorption (at 23°C, 24hrs) ¹¹	0.01	%	ASTM D570
Mold Shrinkage (flow) ᵍ ¹¹	0.2 - 0.3	%	SABIC method
Mold Shrinkage (xflow) ᵍ ¹¹	0.4 - 0.5	%	SABIC method

Table 3 of 7

13 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	268	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	275	°C	ASTM D648
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	270	°C	ISO 75/Af
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	276	°C	ISO 75/Bf
Coefficient of Thermal Expansion (at -40°C to 90°C, flow) ¹¹	0.000012	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 90°C, flow) ¹¹	0.000013	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 90°C, xflow) ¹¹	0.000041	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 90°C, xflow) ¹¹	0.000043	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000013	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.00004	1/°C	ISO 11359-2
Relative Temperature Index (Electrical) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	130	°C	UL 746B

Table 4 of 7

4 rows

Characteristic	Value	Method
Dielectric Constant (at 1.9 GHz) ¹¹	4.3	SABIC method
Dissipation Factor (at 1.9 GHz) ¹¹	0.005	SABIC method
Dielectric Constant (at 5 GHz) ¹¹	4.3	SABIC method
Dissipation Factor (at 5 GHz) ¹¹	0.0058	SABIC method

Table 5 of 7

8 rows

Characteristic	Value	Unit	Method
Izod Impact (Notched, at 23°C) ¹¹	145	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	650	J/m	ASTM D4812
Izod Impact (Notched, 80104, at 23°C) ¹¹	15	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	55	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at -40°C) ¹¹	13.5	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80104, at -40°C) ¹¹	50	kJ/m²	ISO 180/1U
Charpy Impact (at 23°C, V-notch Edgew 80104 sp=62mm) ¹¹	15	kJ/m²	ISO 179/1eA
Charpy Impact (at 23°C, Unnotch Edgew 80104 sp=62mm) ¹¹	55	kJ/m²	ISO 179/1eU

Table 6 of 7