LNP™ THERMOCOMP™ Compound UF00BAS
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP THERMOCOMP UF00BAS compound is based on Polyphthalamide (PPA) resin containing 55% glass fiber. Added features of this grade include: Heat Stabilized. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Powertrain & UTH
- Consumer Electronics
- Displays
- Connectors
- Housings & Enclosures
- Semiconductor Manufacturing
- Switches & Relays
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyphthalamide (PPA)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 15910.0 - 15910.0 MPa
- Additives Included
- Heat Stabilizer, Mold Release Agent
- Heat Stabilizer
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Good Mold Release
- Heat Stabilized
- High Modulus
- High Stiffness
- High Temperature Resistance
- No Added PFAS
- Very Good Heat Resistance
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Automotive Under The Hood
- Cell Phones
- Commercial Appliance
- Computer Components
- Displays
- Electrical Components
- Electrical Enclosure
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹¹ | 227 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.6 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 18870 | MPa | ISO 527 |
| Flexural Stress ¹¹ | 314 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 15910 | MPa | ISO 178 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 246 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 1.8 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 19240 | MPa | ASTM D638 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 338 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 17300 | MPa | ASTM D790 |
Table 2 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.21 | % | ISO 62 |
| Specific Gravity ¹¹ | 1.64 | — | ASTM D792 |
| Density ¹¹ | 1.6 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.13 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.4 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 - 3 | % | ASTM D955 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 293 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 272 | °C | ISO 75/Af |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 289 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 270 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000028 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000035 | 1/°C | ASTM D696 |
Table 4 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 34 | kJ/m² | ISO 180/1U |
| Multi-Axial Impact ¹¹ | 1 | J | ISO 6603 |
| Izod Impact (Notched, at 23°C) ¹¹ | 82 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 291 | J/m | ASTM D4812 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 5 | J | ASTM D3763 |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 - 150 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 | % |
| Melt Temperature ⁷ | 315 - 330 | °C |
| Front - Zone 3 Temperature ⁷ | 325 - 340 | °C |
| Middle - Zone 2 Temperature ⁷ | 315 - 325 | °C |
| Rear - Zone 1 Temperature ⁷ | 310 - 320 | °C |
| Mold Temperature ⁷ | 140 - 165 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |