LNP™ THERMOCOMP™ Compound AF002
- Chemical Family
- Acrylonitrile Butadiene Styrene (ABS)Styrenics
SABIC's Specialties Business LNP THERMOCOMP AF002 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 10% glass fiber. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
- Glazing & Window Elements
- Interior Fixtures
- Artificial Turf
- Consumer Electronics
- Displays
- Non-Food Consumer Packaging
- Applicators & Accessories
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Styrenics
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Acrylonitrile Butadiene Styrene (ABS)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Personal Care
- Printing & Packaging
- Flame Rating
- UL 94 HB
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- High Modulus
- High Stiffness
- No Added PFAS
- Country Availability
- Canada
- Mexico
- USA
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Construction Applications
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 64 | MPa | ISO 527 |
| Tensile Stress (Break) ¹¹ | 66 | MPa | ASTM D638 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 54 | MPa | ISO 527 |
| Tensile Strain (Break) ¹¹ | 2.7 | % | ISO 527 |
| Tensile Strain (Break) ¹¹ | 2.5 | % | ASTM D638 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 54 | MPa | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 4130 | MPa | ASTM D638 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 2.7 | % | ISO 527 |
| Flexural Stress ¹¹ | 107 | MPa | ISO 178 |
| Flexural Stress ¹¹ | 105 | MPa | ASTM D790 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2.8 | % | ISO 527 |
| Flexural Modulus ¹¹ | 4500 | MPa | ISO 178 |
Table 2 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow) ᵍ ¹¹ | 0.2 - 0.4 | % | SABIC method |
| Density ¹¹ | 1.1 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.10E+00 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.111 | g/cm³ | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.33 | % | ISO 62-1 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.41 | % | ISO 294 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.4 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.4 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.38 | % | ISO 294 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.38 | % | ISO 62 |
Table 3 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00006 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00012 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 102 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 95 | °C | ISO 75/Af |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 101 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 92 | °C | ASTM D648 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 60 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 60 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 60 | °C | UL 746B |
Table 4 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 23 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 320 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 80 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹ | 15 | J | ASTM D3763 |
| Multi-Axial Impact ¹¹ | 3 | J | ISO 6603 |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.05 - 0.1 | % |
| Melt Temperature ⁷ | 260 | °C |
| Front - Zone 3 Temperature ⁷ | 265 - 275 | °C |
| Middle - Zone 2 Temperature ⁷ | 230 - 245 | °C |
| Rear - Zone 1 Temperature ⁷ | 205 - 215 | °C |
| Mold Temperature ⁷ | 70 - 80 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |
Table 6 of 6
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94HB Flame Class Rating) ᵖ | 1.5 | mm | UL 94 |