LNP™ THERMOCOMP™ Compound SF00A
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP THERMOCOMP SF00A compound is based on Nylon 12 resin containing 50% glass fiber. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Powertrain & UTH
- Equipment & Parts
- Consumer Electronics
- Displays
- Housings & Enclosures
- Semiconductor Manufacturing
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polyamide 12 (PA 12)
- Fillers Included
- Glass Fiber
- Additives Included
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Cost Effective
- Good Mold Release
- High Modulus
- High Stiffness
- No Added PFAS
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Automotive Applications
- Automotive Under The Hood
- Cell Phones
- Commercial Appliance
- Computer Components
- Consumer Applications
- Displays
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
13 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 121 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 121 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 1.7 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 1.7 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 12800 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 217 | MPa | ASTM D790 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹ | 217 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 10984 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 113 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 113 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 1.5 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 1.5 | % | ISO 527 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.48 | g/cm³ | ASTM D792 |
| Density ¹¹ | 1.48 | g/cm³ | ISO 1183 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.2 - 0.4 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.8 - 1 | % | ASTM D955 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 176 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 166 | °C | ASTM D648 |
Table 4 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 833 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 160 | J/m | ASTM D256 |
| Multi-Axial Impact ¹¹ | 16 | J | ISO 6603 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 1 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.12 - 0.2 | % |
| Melt Temperature ⁷ | 225 - 240 | °C |
| Front - Zone 3 Temperature ⁷ | 225 - 240 | °C |
| Middle - Zone 2 Temperature ⁷ | 220 - 230 | °C |
| Rear - Zone 1 Temperature ⁷ | 215 - 225 | °C |
| Mold Temperature ⁷ | 70 - 80 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |