CYCOLOY™ FR Resin CS9610
SABIC's Specialties Business CYCOLOY CS9610 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an injection moldable low smoke, non chlorinated/brominated flame retardant grade. It has good mechanical and impact properties and has a UL94 V0@2.0mm and 5VB@2.0mm flame rating.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Electrical & Electronic Systems
- Glazing & Window Elements
- Interior Fixtures
- Consumer Electronics
- Displays
- Batteries
- Connectors
- Housings & Enclosures
- Switches & Relays
Product Families
- Blends & Alloys
Other characteristics
- Brand
- CYCOLOY™ FR Resin
- Density
- 1200.0 - 1200.0 kg/m³
- Polymer Name
- PC/ABS Alloy
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Processing Methods
- Injection Molding
- Note
ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Flame Rating
- UL 94 5VB
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Bromine-free
- Chlorine-free
- Low Toxicity
- Additives Included
- Flame Retardant
- Material Features
- Flame Retardant
- High Impact Resistance
- Low Smoke Emission
- Low Toxicity
- Non-brominated
- Non-chlorinated
- Unreinforced
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Building Materials
- Cell Phones
- Computer Components
- Construction Applications
- Displays
- EV Battery Modules
- Electrical Components
- Electrical/Electronic Applications
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 64 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 62 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 5 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 55 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2600 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 98 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2440 | MPa | ASTM D790 |
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 62 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 50 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 4.8 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | min. 45 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2400 | MPa | ISO 527 |
Table 2 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.20E+00 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ʰ ¹¹ | 0.4 - 0.6 | % | SABIC method |
| Melt Flow Rate (at 260°C, 5.0 kgf) ¹¹ | 15 | g/10 min | ASTM D1238 |
| Melt Volume Rate (at 260°C, 5.0 kg) ¹¹ | 12 | cm³/10 min | ISO 1133 |
Table 3 of 6
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 118 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 105 | °C | ASTM D648 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 124 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 127 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 106 | °C | ISO 75/Af |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 90 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 90 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 90 | °C | UL 746B |
Table 4 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 800 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 72 | J | ASTM D3763 |
| Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ | 45 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*3, at -30°C) ¹¹ | 15 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 45 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 15 | kJ/m² | ISO 179/1eA |
Table 5 of 6
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 90 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.04 | % |
| Melt Temperature ⁷ | 270 - 300 | °C |
| Nozzle Temperature ⁷ | 265 - 300 | °C |
| Front - Zone 3 Temperature ⁷ | 265 - 300 | °C |
| Middle - Zone 2 Temperature ⁷ | 260 - 300 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 300 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 60 - 90 | °C |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa |
| Screw Speed ⁷ | 40 - 70 | rpm |
Table 6 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VB Flame Class Rating) ᵖ | min. 2 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 2 | mm | UL 94 |
| NBS Smoke Density (Flaming, Dmax) ᵖ | 225 | — | ASTM E662 |
| NBS Smoke Density (Flaming, Ds 1.5 min) ᵖ | 40 | — | ASTM E662 |
| NBS Smoke Density (Flaming, Ds 4 min) ᵖ | 150 | — | ASTM E662 |