LNP™ THERMOTUF™ Compound VC006
- Chemical Family
- Polyamides
SABIC's Specialties Business LNP™ THERMOTUF™ VC006 compound is based on Super Tough Nylon resin containing 30% carbon fiber. Added features of this grade include: Impact Modified, Electrically Conductive.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Lawn & Garden
- Consumer Goods — Sports & Recreation
Building & Construction — Building Envelope & Roofing
- Glazing & Window Elements
Building & Construction — Building Materials
- Interior Fixtures
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Building & Construction — Decorative Materials & Finishes
- Artificial Turf
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
- Displays
Industrial — Military & Defense
- Advanced Materials
Printing & Packaging — Packaging
- Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
- Applicators & Accessories
Electrical & Electronics — Parts & Components
- Connectors
- Switches & Relays
Product Families
Plastics — Engineering & Specialty Polymers
- Polyamides
Other characteristics
- Brand
- LNP™ THERMOTUF™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Carbon Fiber
- Flexural Modulus
- 15530.0 - 15530.0 MPa
- Additives Included
- Impact Modifier
- Processing Methods
- Injection Molding
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Markets
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Personal Care
- Printing & Packaging
- Technology
- Plastics
- Material Features
- Electrically Conductive
- High Impact Resistance
- High Stiffness
- High Strength
- Impact Modified
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Plastics and Elastomers End Uses
- Appliances
- Building Materials
- Cell Phones
- Commercial Appliance
- Computer Components
- Construction Applications
- Consumer Applications
- Containers
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
20 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹¹ | 157 | MPa | ASTM D638 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 197 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹¹ | 2.4 | % | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 197 | MPa | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 16370 | MPa | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 20700 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 2.9 | % | ASTM D638 |
| Flexural Stress ¹¹ | 241 | MPa | ASTM D790 |
| Flexural Stress ¹¹ | 284 | MPa | ISO 178 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 2.9 | % | ASTM D638 |
| Flexural Modulus ¹¹ | 14550 | MPa | ASTM D790 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 293 | MPa | ASTM D790 |
Table 2 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.21 | g/cm³ | ASTM D792 |
| Density ¹¹ | 1.22 | g/cm³ | ASTM D792 |
| Specific Gravity ¹¹ | 1.21 | — | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.62 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.25 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 1 | % | ASTM D955 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.95 | % | ISO 62 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 250 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 261 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.000034 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.000102 | 1/°C | ASTM D696 |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 258 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 240 | °C | ISO 75/Af |
Table 4 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, at 23°C) ¹¹ | 843 | J/m | ASTM D4812 |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 1070 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) ¹¹ | 149 | J/m | ASTM D256 |
| Izod Impact (Notched, at 23°C) ¹¹ | 207 | J/m | ASTM D256 |
| Multi-Axial Impact ¹¹ | 7 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 32 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 74 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 20 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 | °C |
| Drying Time ⁷ | 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.15 | % |
| Melt Temperature ⁷ | 280 - 295 | °C |
| Front - Zone 3 Temperature ⁷ | 295 - 305 | °C |
| Middle - Zone 2 Temperature ⁷ | 275 - 290 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 270 | °C |
| Mold Temperature ⁷ | 95 - 110 | °C |
| Back Pressure ⁷ | 0.2 - 0.3 | MPa |
| Screw Speed ⁷ | 30 - 60 | rpm |