LNP™ ELCRIN™ WF0061iQ

Chemical Family: Polyesters

SABIC's Specialties Business LNP ELCRIN WF0061iQ compound is based on Polybutylene terephthalate (PBT) resin utilizing ELCRIN iQ upcycling technology containing minimum 25% Post-Consumer Recycling (PCR) weight content and 30% glass fiber. Added features of this grade include: Non-Chlorinated, Non-Brominated Flame Retardant, UL94V0 and 5VA Flame Rating, Excellent Chemical Resistance. This is a good candidate for a variety of applications needing a more sustainable FR and PBT solution.

Other characteristics

Brand: LNP™ ELCRIN
Density: 1560.0 - 1560.0 kg/m³
Polymer Name: Polybutylene Terephthalate (PBT)
Labeling Claims: Bromine-free, Chlorine-free, Contains PCR Resin, Recyclable, Recycled, Sustainable; Bromine-free; Chlorine-free; Contains PCR Resin; Recyclable; Recycled; Sustainable
Fillers Included: Glass Fiber
Additives Included: Flame Retardant
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Personal Care
Printing & Packaging
Flame Rating: UL 94 5VA
UL 94 5VB
UL 94 V0
Technology: Plastics
Material Features: Chemical Resistant
Flame Retardant
High Stiffness
Non-brominated
Non-chlorinated
Recyclable
Country Availability: Canada
China (Mainland)
Mexico
USA
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Appliances
Automotive Applications
Automotive Interior Parts
Cell Phones
Commercial Appliance
Computer Components
Connectors
Consumer Applications
Plastics and Elastomers Functions: Resin

Technical data

Table 1 of 7

16 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	105	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	105	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	2	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	2	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	11000	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	165	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	165	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	9600	MPa	ASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹	108	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	108	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	2	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2	%	ISO 527

Table 2 of 7

7 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.56	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.28	%	SABIC method
Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹	0.57	%	SABIC method
Density ¹¹	1.56	g/cm³	ISO 1183
Water Absorption (at 23°C, saturated) ¹¹	0.23	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.09	%	ISO 62
Melt Volume Rate (at 250°C, 5 kg) ¹¹	16	cm³/10 min	ISO 1133

Table 3 of 7

8 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	200	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	214	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000024	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.00008	1/°C	ASTM E831
Ball Pressure Test (at 123°C to 127°C) ¹¹	Pass	—	IEC 60695-10-2
Relative Temperature Index (Electrical) ᵖ ¹¹	75	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	75	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	75	°C	UL 746B

Table 4 of 7

5 rows

Characteristic	Value	Unit	Method
Volume Resistivity ¹¹	15	Ω.cm	ASTM D257
Hot Wire Ignition (PLC 1) ᵖ ¹¹	min. 0.8	mm	UL 746A
Hot Wire Ignition (PLC 0) ᵖ ¹¹	min. 3	mm	UL 746A
High Ampere Arc Ignition (PLC 0) ᵖ ¹¹	min. 0.8	mm	UL 746A
Comparative Tracking Index ᵖ ¹¹	600	V	IEC 60112

Table 5 of 7