NORYL™ Resin PKN4752
SABIC's Specialties Business NORYL™ PKN4752 resin is a non-reinforced, translucent, high heat blend of polyphenylene ether (PPE) + general purpose polystyrene (GPPS). This extrudable and injection moldable grade exhibits high heat resistance, dimensional stability, and appears translucent with a yellow tint in the natural color. NORYL™ PKN4752 resin is an excellent candidate for high performance packaging in food, electronics, and healthcare. *See NORYL™ PKN4752F resin for FDA food compliant version.
Product families
Applications
Industrial — Chemical & Industrial Manufacturing
- Equipment & Parts
Electrical & Electronics — Devices & Assemblies
- Industrial Automation
Printing & Packaging — Packaging
- Food & Beverage Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
Product Families
Plastics — Engineering & Specialty Polymers
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1080.0 - 1080.0 kg/m³
- Polymer Name
- PPE/GPPS Alloy
- Processing Methods
- Extrusion, Profile Extrusion, Sheet Extrusion
- Note
ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.. ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Translucent
- Transparent
- Markets
- Electrical & Electronics
- Industrial
- Printing & Packaging
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Amorphous
- Dimensional Stability
- Food Contact Acceptable
- High Hydrolytic Stability
- High Temperature Resistance
- Low Moisture Absorption
- Low Shrinkage
- Low Specific Gravity
- Country Availability
- Canada
- China (Mainland)
- Mexico
- USA
- Certifications and Compliance
- FDA Compliant
- Plastics and Elastomers End Uses
- Audio Equipment
- Bottles
- Consumer Applications
- Electrical/Electronic Applications
- Electronic Components
- Flexible Packaging
- Food Containers
- Food Packaging
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Profile Extrusion
- Sheet Extrusion
Technical data
Table 1 of 6
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 86 | MPa | ISO 527 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 86 | MPa | ASTM D638 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 6 | % | ISO 527 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 73 | MPa | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 3100 | MPa | ISO 527 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 6.00E+00 | % | ASTM D638 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 130 | MPa | ISO 178 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 15 | % | ASTM D638 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2950 | MPa | ISO 178 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 3000 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 144 | MPa | ASTM D790 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 136 | MPa | ASTM D790 |
Table 2 of 6
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.08 | g/cm³ | ISO 1183 |
| Specific Gravity ¹¹ | 1.08 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.6 - 0.9 | % | SABIC method |
Table 3 of 6
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate A/50) ¹¹ | 174 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 163 | °C | ISO 75/Be |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 147 | °C | ISO 75/Ae |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 173 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 160 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 151 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 151 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000063 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000558 | 1/°C | ASTM E831 |
Table 4 of 6
14 rows| Characteristic | Value | Unit |
|---|---|---|
| Adapter Temperature | 240 - 265 | °C |
| Barrel - Zone 1 Temperature | 205 - 225 | °C |
| Barrel - Zone 2 Temperature | 215 - 240 | °C |
| Barrel - Zone 3 Temperature | 240 - 265 | °C |
| Barrel - Zone 4 Temperature | 240 - 265 | °C |
| Die Temperature | 240 - 265 | °C |
| Drying Temperature | 70 - 80 | °C |
| Drying Time | 2 - 4 | Hrs |
| Drying Time (Cumulative) | 8 | Hrs |
| Maximum Moisture Content | 0 | % |
| Melt Temperature | 265 - 275 | °C |
| Roll Stack Temperature - Bottom | 105 - 120 | °C |
Table 5 of 6
11 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature | 80 - 95 | °C |
| Drying Time | 2 - 4 | Hrs |
| Melt Temperature | 280 - 300 | °C |
| Barrel - Zone 1 Temperature | 215 - 240 | °C |
| Barrel - Zone 2 Temperature | 225 - 250 | °C |
| Barrel - Zone 3 Temperature | 250 - 275 | °C |
| Barrel - Zone 4 Temperature | 250 - 275 | °C |
| Hopper Temperature | 50 - 70 | °C |
| Adapter Temperature | 250 - 275 | °C |
| Die Temperature | 250 - 275 | °C |
| Calibrator Temperature | 60 - 80 | °C |
Table 6 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 2 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 2 | kJ/m² | ISO 179/1eA |
| Izod Impact (Notched, at 23°C) ¹¹ | 32 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 6 | J | ASTM D3763 |