To catalogue
LEXAN™ VISUALFX™ Resin FXD144R
- Chemical Family
- Polycarbonate (PC)
Transparent/translucent medium viscosity grade for light diffusion. FDA compliant. Color package may affect performance.
Product families
Applications
Applications
- Consumer Goods — Appliances & Electronics
Electrical & Electronics — Devices & Assemblies
- Consumer Electronics
Product Families
Plastics — Engineering & Specialty Polymers
- High Performance Thermoplastics
- Polycarbonates
Other characteristics
- Brand
- LEXAN™ VISUALFX™ Resin
- Polymer Name
- Polycarbonate (PC)
- Additives Included
- Mold Release Agent
- Processing Methods
- Injection Molding
- Note
ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- Color
- Translucent
- Transparent
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- Material Features
- Excellent Aesthetics
- Food Contact Acceptable
- Good Aesthetics
- Good Mold Release
- Good Surface Appearance
- High Light Diffusion
- Medium Viscosity
- Translucent
- Certifications and Compliance
- FDA Compliant
- Plastics and Elastomers End Uses
- Appliances
- Consumer Applications
- Home Appliances
- Kitchen & Coffee Machines
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
15 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 63 | MPa | ISO 527 |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 61 | MPa | ASTM D638 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 70 | MPa | ISO 527 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 68 | MPa | ASTM D638 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 6 | % | ISO 527 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 6.2 | % | ASTM D638 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 110 | % | ISO 527 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 128 | % | ASTM D638 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2350 | MPa | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 2300 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 93 | MPa | ASTM D790 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 90 | MPa | ISO 178 |
Table 2 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹¹ | 1.19 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ʰ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 10.8 | g/10 min | ASTM D1238 |
| Mold Shrinkage (on Tensile Bar, flow) ʰ ¹¹ | 0.5 - 0.7 | % | SABIC method |
| Density ¹¹ | 1.2 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.35 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.15 | % | ISO 62 |
| Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ | 11 | cm³/10 min | ISO 1133 |
Table 3 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 126 | °C | ASTM D648 |
| Thermal Conductivity ¹¹ | 0.2 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 141 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 142 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 136 | °C | ISO 75/Be |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 125 | °C | ISO 75/Ae |
Table 4 of 7
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Volume Resistivity ¹¹ | min. 1.E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) ¹¹ | 2.7 | — | IEC 60250 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.001 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.01 | — | IEC 60250 |
| Comparative Tracking Index ¹¹ | 250 | V | IEC 60112 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.7 | — | IEC 60250 |
Table 5 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹¹ | 854 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 76 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*3, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*3, at -30°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ | 7.00E+01 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*3, at -30°C) ¹¹ | 12 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 73 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 14 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 120 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Maximum Moisture Content ⁷ | 0.02 | % |
| Melt Temperature ⁷ | 280 - 310 | °C |
| Nozzle Temperature ⁷ | 270 - 290 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 310 | °C |
| Middle - Zone 2 Temperature ⁷ | 270 - 290 | °C |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 80 - 110 | °C |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Oxygen Index (LOI) | 25 | % | ISO 4589 |