ULTEM™ Resin 2410
- Chemical Family
- Polyetherimide (PEI)Polyimides (PI)
SABIC's Specialties Business 40% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Other characteristics
- Brand
- ULTEM™ Resin
- Polymer Name
- Polyether Imide (PEI)
- Fillers Included
- Glass Fiber
- Additives Included
- Flame Retardant
- Processing Methods
- Injection Molding
- Note
ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.. ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Healthcare & Pharma
- Industrial
- Personal Care
- Printing & Packaging
- Availability
ULTEM™ resin is available in transparent and opaque custom colors, and can be glass filled for added stiffness.
- Flame Rating
- UL 94 5VA
- UL 94 V0
- Key Benefits
- Heat Resistance
- Dimensional Stability
- Dielectric Performance
- Miniaturization and Thin Wall
- Resilience
- Technology
- Plastics
- Labeling Claims
- Bio-based
- Confirms to ECO-Label
- Low Toxicity
- No Added PFAS
- Sustainable
Technical data
Table 1 of 7
14 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Taber Abrasion (CS-17, 1 kg) | 20 | mg/1000cy | SABIC method |
| Tensile Stress (Yield, Type I, 5 mm/min) | 186 | MPa | ASTM D638 |
| Tensile Stress (Break, 5 mm/min) | 180 | MPa | ISO 527 |
| Tensile Stress (Break, Type I, 5 mm/min) | 179 | MPa | ASTM D638 |
| Tensile Strain (Break, 5 mm/min) | 2 | % | ISO 527 |
| Tensile Strain (Break, Type I, 5 mm/min) | 2.5 | % | ASTM D638 |
| Tensile Modulus (at 1 mm/min) | 11500 | MPa | ISO 527 |
| Tensile Modulus (at 5 mm/min) | 11720 | MPa | ASTM D638 |
| Flexural Stress (Break, 2 mm/min) | 240 | MPa | ISO 178 |
| Flexural Stress (Break, 2.6 mm/min, 100 mm span) | 2.41E+02 | MPa | ASTM D790 |
| Flexural Modulus (at 2 mm/min) | 10000 | MPa | ISO 178 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) | 11720 | MPa | ASTM D790 |
Table 2 of 7
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity | 1.61 | — | ASTM D792 |
| Water Absorption (at 23°C, 24hrs) | 0.13 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) | 0.8 | % | ISO 62-1 |
| Water Absorption (at 23°C, saturated) | 0.9 | % | ASTM D570 |
| Mold Shrinkage (flow, 3.2 mm) | 0.1 - 0.3 | % | SABIC method |
| Melt Flow Rate (at 337°C, 6.6 kgf) | 5.2 | g/10 min | ASTM D1238 |
| Mold Shrinkage (on Tensile Bar, flow) | 0.1 - 0.3 | % | SABIC method |
| Density | 1.61 | g/cm³ | ISO 1183 |
| Moisture Absorption (at 23°C, 50% RH) | 0.4 | % | ISO 62 |
| Melt Volume Rate (at 360°C, 5.0 kg) | 7 | cm³/10 min | ISO 1133 |
Table 3 of 7
19 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Vicat Softening Temperature (Rate B/50) | 217 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) | 234 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) | 215 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) | 212 | °C | ASTM D648 |
| Thermal Conductivity | 0.29 | W/m-°C | ISO 8302 |
| Coefficient of Thermal Expansion (at -20°C to 150°C, flow) | 0.000014 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 150°C, flow) | 0.000014 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 150°C, xflow) | 0.000045 | 1/°C | ISO 11359-2 |
| Ball Pressure Test (at 123°C to 127°C) | Pass | — | IEC 60695-10-2 |
| Relative Temperature Index (Electrical) ᵖ | 170 | °C | UL 746B |
| Relative Temperature Index (Electrical) ᵖ | 105 | °C | UL 746B |
| Vicat Softening Temperature (Rate A/50) | 230 | °C | ISO 306 |
Table 4 of 7
21 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| High Voltage Arc Track Rate (PLC) | 4 | PLC Code | UL 746A |
| Relative Permittivity (1 kHz) | 3.7 | — | ASTM D150 |
| Volume Resistivity | 1.00E+15 | Ω.cm | IEC 60093 |
| Volume Resistivity | 1.50E+16 | Ω.cm | ASTM D257 |
| Dielectric Strength (in oil, at 1.6mm) | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength (in oil, at 1.6mm) | 24 | kV/mm | ASTM D149 |
| Dissipation Factor (at at 1 kHz) | 0.002 | — | ASTM D150 |
| Comparative Tracking Index (UL, PLC) | 4 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) | 5 | PLC Code | UL 746A |
| Surface Resistivity (ROA) | min. 1.E+15 | Ω | IEC 60093 |
| Dielectric Strength (in oil, at 0.8mm) | 35 | kV/mm | IEC 60243-1 |
| Hot Wire Ignition (PLC 0) | min. 1.5 | mm | UL 746A |
Table 5 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 80*10*4, at 23°C) | 35 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, at 23°C) | 427 | J/m | ASTM D4812 |
| Izod Impact (Notched, at 23°C) | 112 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at -30°C) | 35 | kJ/m² | ISO 180/1U |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) | 40 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) | 40 | kJ/m² | ISO 179/1eU |
Table 6 of 7
21 rows| Characteristic | Value | Unit |
|---|---|---|
| Back Pressure | 0.3 - 0.7 | MPa |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | Hrs |
| Drying Time (Cumulative) | 24 | Hrs |
| Front - Zone 3 Temperature | 345 - 400 | °C |
| Front - Zone 3 Temperature | 380 - 420 | °C |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 350 - 400 | °C |
| Melt Temperature | 370 - 410 | °C |
| Middle - Zone 2 Temperature | 340 - 400 | °C |
| Middle - Zone 2 Temperature | 370 - 410 | °C |
| Mold Temperature | 135 - 165 | °C |
Table 7 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized (94-5VA Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.25 | mm | UL 94 |
| Oxygen Index (LOI) ᵖ | 48 | % | ISO 4589 |
| Oxygen Index (LOI) ᵖ | 54 | % | ASTM D2863 |
| NBS Smoke Density (Flaming, Ds 4 min) ᵖ | 1 | — | ASTM E662 |
| Glow Wire Flammability Index (passes at 960°C) ᵖ | 3.2 | mm | IEC 60695-2-12 |