LNP™ VERTON™ Compound RV00AE
- Chemical Family
- Polyamides
LNP™ VERTON™ Compound RV00AE is a compound based on polyamide 66 (nylon 66) resin containing 50% long glass fiber. Added features of this grade include easy molding and structural integrity. This compound offers high stiffness and strength, making it ideal for various injection molding applications. Suitable for automotive exteriors, building components, sports and leisure equipment, home appliances, and commercial appliances, LNP™ VERTON™ Compound RV00AE ensures durability and performance across diverse industrial applications. Its enhanced structural properties and ease of molding contribute to its reliability and efficiency in demanding environments
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Structural Components
- Industrial Automation
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Processing Methods
- Injection Molding
- Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. (2) UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. (3) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. (4) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Easy To Mold
- Good Processability
- High Stiffness
- High Strength
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Building Materials
- Commercial Appliance
- Home Appliances
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
11 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, Type I, 5 mm/min) ¹ | 219.0 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹ | 2.1 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹ | 15660.0 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹ | 362.0 | MPa | ASTM D790 |
| Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹ | 359.0 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹ | 13200.0 | MPa | ASTM D790 |
| Tensile Stress (Break, 5 mm/min) ¹ | 216.0 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹ | 2.3 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 14450.0 | MPa | ISO 527 |
| Flexural Stress ¹ | 342.0 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹ | 13310.0 | MPa | ISO 178 |
Table 2 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹ | 1.59 | — | ASTM D792 |
| Density ¹ | 1.59 | g/cm³ | ASTM D792 |
| Moisture Absorption (23°C/50% RH/24 hrs) ¹ | 0.64 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ³ | 0.1 - 0.3 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ³ | 0.4 - 0.6 | % | ASTM D955 |
| Moisture Absorption (23°C / 50% RH) ¹ | 1.2 | % | ISO 62 |
Table 3 of 7
9 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹ | 226.0 | °C | ASTM D648 |
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 223.0 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹ | 2.0e-05 | 1/°C | ASTM D696 |
| Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹ | 7.5e-05 | 1/°C | ASTM D696 |
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 224.0 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 222.0 | °C | ISO 75/Af |
| Relative Temperature Index (Elec) ² | 105.0 | °C | UL 746B |
| Relative Temperature Index (Mech with impact) ² | 110.0 | °C | UL 746B |
| Relative Temperature Index (Mech w/o impact) ² | 110.0 | °C | UL 746B |
Table 4 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Arc Resistance (Tungsten) ² | 6.0 | PLC Code | ASTM D495 |
| Comparative Tracking Index (UL) ² | 0.0 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI, PLC 0) ² | min. 1.5 | mm | UL 746A |
| Hot-Wire Ignition (HWI, PLC 2) ² | min. 0.75 | mm | UL 746A |
| High Amp Arc Ignition (HAI, PLC 0) ² | min. 0.75 | mm | UL 746A |
| High Voltage Arc Track Rate ² | 0.0 | PLC Code | UL 746A |
Table 5 of 7
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 23°C) ¹ | 1260.0 | J/m | ASTM D4812 |
| Izod Impact (Notched, 23°C) ¹ | 392.0 | J/m | ASTM D256 |
| Multiaxial Impact ¹ | 8.0 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹ | 15.0 | J | ASTM D3763 |
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 83.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 42.0 | kJ/m² | ISO 180/1A |
Table 6 of 7
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁴ | 80.0 | °C |
| Drying Time ⁴ | 2 - 4 | Hrs |
| Drying Time (Cumulative) ⁴ | 12.0 | Hrs |
| Minimum Moisture Content ⁴ | 0.15 | % |
| Maximum Moisture Content ⁴ | 0.25 | % |
| Melt Temperature ⁴ | 290 - 305 | °C |
| Front - Zone 3 Temperature ⁴ | 290 - 300 | °C |
| Middle - Zone 2 Temperature ⁴ | 290 - 300 | °C |
| Rear - Zone 1 Temperature ⁴ | 280 - 295 | °C |
| Mold Temperature ⁴ | 95 - 110 | °C |
| Back Pressure ⁴ | 0.2 - 0.3 | MPa |
| Screw Speed ⁴ | 30 - 60 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized 94HB Flame Class Rating ² | min. 0.75 | mm | UL 94 |