LNP™ VERTON™ Compound RV007ESS
- Chemical Family
- Polyamides
LNP™ VERTON™ Compound RV007ESS is a compound based on polyamide 66 (nylon 66) resin containing 35% long glass fiber. Added features include easy molding, structural integrity, and heat stabilization. This compound is designed for injection molding and offers high stiffness and strength, making it ideal for automotive exteriors, building components, sports and leisure equipment, home appliances, and commercial appliances. Its enhanced molding properties and durability ensure reliable performance across various industrial applications.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Structural Components
- Industrial Automation
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 9880.0 - 9880.0 MPa
- Processing Methods
- Injection Molding
- Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. (2) UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. (3) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Easy To Mold
- Good Processability
- Heat Stabilized
- High Stiffness
- High Strength
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Building Materials
- Commercial Appliance
- Home Appliances
- Sporting Goods
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 7
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹ | 204.0 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹ | 214.0 | MPa | ISO 527 |
| Tensile Strain (Break) ¹ | 2.1 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 11970.0 | MPa | ISO 527 |
| Flexural Stress ¹ | 309.0 | MPa | ISO 178 |
| Flexural Modulus ¹ | 10240.0 | MPa | ISO 178 |
| Flexural Modulus ¹ | 9880.0 | MPa | ASTM D790 |
Table 2 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.42 | g/cm³ | ISO 1183 |
| Density ¹ | 1.42 | g/cm³ | ASTM D792 |
| Moisture Absorption (23°C/50% RH/24 hrs) ¹ | 0.97 | % | ASTM D570 |
Table 3 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 245.0 | °C | ASTM D648 |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 252.0 | °C | ISO 75/Af |
| Relative Temperature Index (Elec) ² | 95.0 | °C | UL 746B |
| Relative Temperature Index (Mech with impact) ² | 65.0 | °C | UL 746B |
| Relative Temperature Index (Mech w/o impact) ² | 75.0 | °C | UL 746B |
Table 4 of 7
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Hot-Wire Ignition (HWI, PLC 0) ¹ | min. 3 | mm | UL 746A |
| Hot-Wire Ignition (HWI, PLC 3) ¹ | min. 1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI, PLC 0) ¹ | min. 1.5 | mm | UL 746A |
| High Voltage Arc Track Rate ¹ | 0.0 | PLC Code | UL 746A |
| Arc Resistance (Tungsten) ¹ | 6.0 | PLC Code | ASTM D495 |
Table 5 of 7
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 23°C) ¹ | 277.0 | J/m | ASTM D256 |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 29.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched 80*10*4 -40°C) ¹ | 25.0 | kJ/m² | ISO 180/1A |
Table 6 of 7
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 80.0 | °C |
| Drying Time ³ | 4.0 | Hrs |
| Maximum Moisture Content ³ | 0.15 - 0.25 | % |
| Melt Temperature ³ | 290 - 305 | °C |
| Front - Zone 3 Temperature ³ | 290 - 300 | °C |
| Middle - Zone 2 Temperature ³ | 290 - 300 | °C |
| Rear - Zone 1 Temperature ³ | 280 - 295 | °C |
| Mold Temperature ³ | 95 - 110 | °C |
| Back Pressure ³ | 0.2 - 0.3 | MPa |
| Screw Speed ³ | 30 - 60 | rpm |
Table 7 of 7
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized 94HB Flame Class Rating | min. 0.75 | mm | UL 94 |