LNP™ ELCRES™ SLX1271SR
- Chemical Family
- Polycarbonate (PC)
LNP™ ELCRES™ SLX1271SR is based on polycarbonate (pc) copolymer resins. This injection moldable and weatherable product offers enhanced UV stabilization and anti-scratch performance. With a medium flow rate of 13g/10min (MFR), it provides good processability and is available in a wide range of high-gloss opaque colors as well as transparent or tinted options. LNP™ ELCRES™ SLX1271SR is targeted for a broad range of mobility exteriors and electronic devices, as well as adjacent applications.
Product families
Applications
- Exterior & Body
- Interior
Product Families
- Polycarbonates
Other characteristics
- Brand
- LNP™ ELCRES
- Polymer Name
- Polycarbonate (PC) Copolymer
- Flexural Modulus
- 2400.0 - 2400.0 MPa
- Processing Methods
- Injection Molding, Sheet Extrusion
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Color
- Opaque
- Transparent
- Markets
- Automotive & Transportation
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Good Processability
- Good Scratch Resistance
- Good Weather Stability
- High Flow
- High Gloss
- Medium Flow
- No Added PFAS
- UV Stabilized
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Electronic Components
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
- Sheet Extrusion
Technical data
Table 1 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, Type I, 50 mm/min) ¹ | 69.6 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹ | 56.9 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹ | 6.7 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹ | 57.5 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹ | 2470.0 | MPa | ASTM D638 |
| Flexural Strength (1.3 mm/min, 50 mm span) ¹ | 103.0 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹ | 2400.0 | MPa | ASTM D790 |
Table 2 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹ | 1.2 | — | ASTM D792 |
| Melt Volume Rate (at 300°C/1.2 kg) ¹ | 11.43 | cm³/10 min | ISO 1133 |
| Mold Shrinkage (flow) ² | 0.7 | % | SABIC method |
| Mold Shrinkage (xflow) ² | 0.71 | % | SABIC method |
Table 3 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹ | 130.0 | °C | ASTM D648 |
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 117.0 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ | 6.5e-05 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ | 6.5e-05 | 1/°C | ASTM E831 |
Table 4 of 6
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Light Transmission (1.0 mm) ¹ | 91.0 | % | ASTM D1003 |
| Haze (1.0 mm) ¹ | 0.6 | % | ASTM D1003 |
| Gloss (at 20 °) ¹ | 105.0 | — | ASTM D2457 |
| Gloss (at 60 °) ¹ | 103.0 | — | ASTM D2457 |
| Gloss (at 85 °) ¹ | 96.0 | — | ASTM D2457 |
Table 5 of 6
12 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, at 23°C) ¹ | 49.3 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 23°C) ¹ | NB | J/m | ASTM D4812 |
| Izod Impact (Notched, at 0°C) ¹ | 47.9 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at 0°C) ¹ | NB | J/m | ASTM D4812 |
| Izod Impact (Notched, at -10°C) ¹ | 47.7 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at -10°C) ¹ | NB | J/m | ASTM D4812 |
| Izod Impact (Notched, at -20°C) ¹ | 47.1 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at -20°C) ¹ | NB | J/m | ASTM D4812 |
| Izod Impact (Notched, at -30°C) ¹ | 46.1 | J/m | ASTM D256 |
| Izod Impact (Unnotched, at -30°C) ¹ | NB | J/m | ASTM D4812 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹ | 76.8 | J | ASTM D3763 |
| Instrumented Dart Impact Ductility (at 23°C) ¹ | 100.0 | % | ASTM D3763 |
Table 6 of 6
7 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 110 - 120 | °C |
| Drying Time ³ | 4 - 6 | Hrs |
| Melt Temperature ³ | 270 - 290 | °C |
| Front - Zone 3 Temperature ³ | 270 - 290 | °C |
| Middle - Zone 2 Temperature ³ | 260 - 280 | °C |
| Rear - Zone 1 Temperature ³ | 250 - 270 | °C |
| Mold Temperature ³ | 80 - 100 | °C |