LNP™ VERTON™ Compound RVL29ESS
- Chemical Family
- Polyamides
LNP™ VERTON™ Compound RVL29ESS combines Polyamide 66 (nylon 66) resin with 45% long glass fiber and 10% PTFE, offering a versatile solution tailored for easy molding, heat stability, wear resistance, and structural integrity. This compound is engineered to excel in demanding applications where high mechanical performance and durability are essential, such as automotive components, industrial machinery, and electrical enclosures. The incorporation of PTFE enhances lubricity, reducing friction and enhancing wear resistance, thereby extending the service life of components. LNP™ VERTON™ Compound RVL29ESS ensures efficient processing during injection molding, maintaining precision and consistency to meet stringent quality standards in complex part geometries.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Exterior & Body
- Structural Components
- Industrial Automation
Product Families
- Polyamides
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polyamide 66 (PA 66)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 8900.0 - 8900.0 MPa, 9000.0 - 9000.0 MPa
- Processing Methods
- Injection Molding
- Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. (2) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.,The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. (3) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Easy To Mold
- Good Processability
- Heat Stabilized
- High Stiffness
- High Strength
- Wear Resistant
- Plastics and Elastomers End Uses
- Automotive Exterior Parts
- Building Materials
- Commercial Appliance
- Home Appliances
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
17 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹ | 231.0 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹ | 2.3 | % | ISO 527 |
| Flexural Stress (Yield, 2 mm/min) ¹ | 361.0 | MPa | ISO 178 |
| Flexural Strain (Break, 2 mm/min) ¹ | 3.2 | % | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹ | 13600.0 | MPa | ISO 178 |
| Flexural Strain (Break, 2 mm/min, 60°C) ¹ | 3.6 | % | ISO 178 |
| Flexural Strain (Break, 2 mm/min), 100°C ¹ | 3.2 | % | ISO 178 |
| Flexural Strain (Break, 2 mm/min, 150°C) ¹ | 3.5 | % | ISO 178 |
| Flexural Strain (Break, 2 mm/min, 200°C) ¹ | 2.7 | % | ISO 178 |
| Flexural Stress (Yield, 2 mm/min, 60°C) ¹ | 300.0 | MPa | ISO 178 |
| Flexural Stress (Yield, 2 mm/min, 100°C) ¹ | 256.0 | MPa | ISO 178 |
| Flexural Stress (Yield, 2 mm/min, 150°C) ¹ | 204.0 | MPa | ISO 178 |
Table 2 of 5
8 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Mold Shrinkage (flow, 24 hrs) ² | 0.13 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ² | 0.48 | % | ISO 294 |
| Wear Factor Washer ¹ | 21.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic Coefficient of Friction ¹ | 0.39 | — | ASTM D3702 Modified: Manual |
| Static COF ¹ | 0.4 | — | ASTM D3702 Modified: Manual |
| Density ¹ | 1.65 | g/cm³ | ISO 1183 |
| Water Absorption (23°C/24hrs) ¹ | 1.19 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) ¹ | 0.46 | % | ISO 62 |
Table 3 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Heat ¹ | 1478.0 | J/kg-K | ASTM E1269 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹ | 2.1e-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹ | 4.9e-05 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 258.0 | °C | ISO 75/Af |
| Thermal Conductivity ¹ | 0.27 | W/m-K | ASTM D5930 |
Table 4 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched 80*10*3 -40°C) ¹ | 28.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 82.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched 80*10*4 -40°C) ¹ | 74.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 30.0 | kJ/m² | ISO 180/1A |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 80.0 | °C |
| Drying Time ³ | 4.0 | Hrs |
| Maximum Moisture Content ³ | 0.15 - 0.25 | % |
| Melt Temperature ³ | 290 - 305 | °C |
| Front - Zone 3 Temperature ³ | 290 - 300 | °C |
| Middle - Zone 2 Temperature ³ | 290 - 300 | °C |
| Rear - Zone 1 Temperature ³ | 280 - 295 | °C |
| Mold Temperature ³ | 95 - 110 | °C |
| Back Pressure ³ | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |