LNP™ VERTON™ Compound MVL36SX0
- Chemical Family
- PolyolefinsPolypropylenes (PP)
LNP™ VERTON™ Compound MVL36SX0 combines polypropylene (PP) resin with 30% long glass fibers and PTFE, offering a robust solution for structural applications. This compound is chemically coupled for enhanced performance, heat stabilized to maintain strength across temperature variations, and boasts wear-resistant properties. It is designed to withstand outdoor conditions with UV stability, making it suitable for automotive exteriors, water management systems, and various industrial applications. LNP™ VERTON™ Compound MVL36SX0 delivers high stiffness and strength, ensuring durability and reliability in sport and leisure equipment, home appliances, and commercial appliances. Ideal for injection molding processes, it provides excellent dimensional stability and processability, meeting the demanding requirements of modern manufacturing.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Equipment & Parts
- Consumer Electronics
Product Families
- Polyolefins
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polypropylene (unspecified)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Chemically Coupled
- Good UV Stability
- Good Weather Stability
- Heat Stabilized
- High Stiffness
- High Strength
- Wear Resistant
- Plastics and Elastomers End Uses
- Automotive Applications
- Commercial Appliance
- Construction Applications
- Home Appliances
- Water Management
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break, 5 mm/min) ¹ | 116.0 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹ | 2.2 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹ | 8500.0 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹ | 133.0 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹ | 6500.0 | MPa | ISO 178 |
Table 2 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.28 | g/cm³ | ISO 1183 |
| Water Absorption (23°C/24hrs) ¹ | 0.01 | % | ISO 62-1 |
| Mold Shrinkage (flow, 24 hrs) ² | 0.37 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ² | 0.73 | % | ISO 294 |
Table 3 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 163.0 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 157.0 | °C | ISO 75/Af |
Table 4 of 5
3 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Multiaxial Impact ¹ | 5.0 | J | ISO 6603 |
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 42.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 17.0 | kJ/m² | ISO 180/1A |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 80.0 | °C |
| Drying Time ³ | 4.0 | Hrs |
| Melt Temperature ³ | 215 - 220 | °C |
| Front - Zone 3 Temperature ³ | 205 - 215 | °C |
| Middle - Zone 2 Temperature ³ | 200 - 210 | °C |
| Rear - Zone 1 Temperature ³ | 195 - 205 | °C |
| Mold Temperature ³ | 30 - 50 | °C |
| Back Pressure ³ | 0.2 - 0.3 | MPa |
| Screw Speed ³ | 30 - 60 | rpm |