LNP™ LUBRICOMP™ Compound DX99699
- Chemical Family
- Polycarbonate (PC)
LNP™ LUBRICOMP™ Compound DX99699 is based on polycarbonate (pc) resin containing glass fiber and PTFE. This grade offers wear resistance and enhanced mold release properties, making it ideal for applications in sport/leisure, personal accessories, home appliances, commercial appliances, electrical devices and displays, and electrical components and infrastructure.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Displays
- Other Parts & Components
Product Families
- Polycarbonates
Other characteristics
- Brand
- LNP™ LUBRICOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Glass Fiber, PTFE
- Glass Fiber
- PTFE
- Flexural Modulus
- 5170.0 - 5170.0 MPa
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Consumer Goods
- Electrical & Electronics
- Technology
- Plastics
- Material Features
- Good Mold Release
- Wear Resistant
- Plastics and Elastomers End Uses
- Commercial Appliance
- Electrical Components
- Electrical Devices
- Electronic Displays
- Home Appliances
- Personal Accessories
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹ | 103.0 | MPa | ASTM D638 |
| Tensile Strain (Break) ¹ | 3 - 4 | % | ASTM D638 |
| Flexural Stress ¹ | 124.0 | MPa | ASTM D790 |
| Flexural Modulus ¹ | 5170.0 | MPa | ASTM D790 |
Table 2 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Specific Gravity ¹ | 1.4 | — | ASTM D792 |
| Water Absorption (23°C/24hrs) ¹ | 0.08 | % | ASTM D570 |
| Matrix Tg ¹ | 149.0 | °C | DMA |
| Melt Volume Rate (at 300°C/1.2 kg) ¹ | 10.0 | cm³/10 min | ISO 1133 |
| Mold Shrinkage (flow, 3.2 mm) ² | 0.25 - 0.35 | % | SABIC method |
Table 3 of 5
1 row| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (1.82 MPa, 6.4 mm, unannealed) ¹ | 145.0 | °C | ASTM D648 |
Table 4 of 5
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 23°C) ¹ | 420.0 | J/m | ASTM D4812 |
| Izod Impact (Notched, 23°C) ¹ | 127.0 | J/m | ASTM D256 |
Table 5 of 5
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 120.0 | °C |
| Drying Time ³ | 4.0 | Hrs |
| Maximum Moisture Content ³ | 0.02 | % |
| Melt Temperature ³ | 305 - 325 | °C |
| Front - Zone 3 Temperature ³ | 320 - 330 | °C |
| Middle - Zone 2 Temperature ³ | 310 - 320 | °C |
| Rear - Zone 1 Temperature ³ | 295 - 305 | °C |
| Mold Temperature ³ | 80 - 110 | °C |
| Back Pressure ³ | 0.2 - 0.3 | MPa |
| Screw Speed ³ | 30 - 60 | rpm |