LNP™ THERMOCOMP™ Compound DF004AXC
- Chemical Family
- Polycarbonate (PC)
LNP™ THERMOCOMP™ Compound DF004AXC is based on polycarbonate (pc) resin filled with 20% glass fiber.
Product families
- Polycarbonates
Other characteristics
- Brand
- LNP™ THERMOCOMP™ Compound
- Polymer Name
- Polycarbonate (PC)
- Fillers Included
- Glass Fiber
- Flexural Modulus
- 5510.0 - 5510.0 MPa
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. ³ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ⁴ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Flame Rating
- UL 94 V1
- UL 94 V2
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- No Added PFAS
- Certifications and Compliance
- UL 94
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 6
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹ | 91.0 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹ | 102.0 | MPa | ISO 527 |
| Tensile Strain (Break) ¹ | 9.5 | % | ASTM D638 |
| Tensile Strain (Break) ¹ | 8.0 | % | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹ | 5510.0 | MPa | ASTM D638 |
| Flexural Stress ¹ | 149.0 | MPa | ASTM D790 |
| Flexural Stress ¹ | 148.0 | MPa | ISO 178 |
| Flexural modulus ¹ | 5510.0 | MPa | ASTM D790 |
| Tensile Modulus (at 1 mm/min) ¹ | 6000.0 | MPa | ISO 527 |
| Flexural Modulus ¹ | 6000.0 | MPa | ISO 178 |
Table 2 of 6
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.35 | g/cm³ | ASTM D792 |
| Density ¹ | 1.35 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C/50% RH/24 hrs) ¹ | 0.1 | % | ASTM D570 |
| Mold Shrinkage (flow, 24 hrs) ³ | 0.2 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ³ | 0.2 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ³ | 0.5 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ³ | 0.45 | % | ISO 294 |
Table 3 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, 3.2 mm, unannealed) ¹ | 144.0 | °C | ASTM D648 |
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 139.0 | °C | ASTM D648 |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 142.0 | °C | ISO 75/Af |
| Relative Temperature Index (Elec) ² ¹ | 80.0 | °C | UL 746B |
| Relative Temperature Index (Mech with impact) ² ¹ | 80.0 | °C | UL 746B |
| Relative Temperature Index (Mech w/o impact) ² ¹ | 80.0 | °C | UL 746B |
Table 4 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Unnotched, 23°C) ¹ | 961.0 | J/m | ASTM D4812 |
| Izod Impact (Notched, 23°C) ¹ | 133.0 | J/m | ASTM D256 |
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 61.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 8.0 | kJ/m² | ISO 180/1A |
Table 5 of 6
10 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁴ | 120.0 | °C |
| Drying Time ⁴ | 4.0 | Hrs |
| Maximum Moisture Content ⁴ | 0.02 | % |
| Melt Temperature ⁴ | 305 - 325 | °C |
| Front - Zone 3 Temperature ⁴ | 320 - 330 | °C |
| Middle - Zone 2 Temperature ⁴ | 310 - 320 | °C |
| Rear - Zone 1 Temperature ⁴ | 295 - 305 | °C |
| Mold Temperature ⁴ | 80 - 110 | °C |
| Back Pressure ⁴ | 0.2 - 0.3 | MPa |
| Screw Speed ⁴ | 30 - 60 | rpm |
Table 6 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| UL Recognized 94V-1 Flame Class Rating ² ¹ | 3.0 | mm | UL 94 |
| UL Recognized 94V-2 Flame Class Rating ² ¹ | 1.5 | mm | UL 94 |