LNP™ VERTON™ Compound PX06419

Chemical Family: Polyamides

LNP™ VERTON™ Compound PX06419 combines Polyamide 6 (Nylon 6) resin with 50% long glass fiber and proprietary fillers, emphasizing heat stabilization and structural strength. Tailored for demanding applications in automotive exteriors, building components, and across various industrial sectors, this compound excels in providing high stiffness and strength without intentional PFAS additives. With its optimized formulation including both glass fiber and proprietary fillers,LNP™ VERTON™ Compound PX06419 ensures robust performance during injection molding processes. It is ideal for sport and leisure equipment, home appliances, and commercial appliances, delivering reliability and endurance where durability and performance are paramount.

Product families

Applications

Consumer Goods — Appliances & Electronics
Consumer Goods — Sports & Recreation

Automotive & Transportation — Automotive

Exterior & Body

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Other characteristics

Brand: LNP™ VERTON™ Compound
Polymer Name: Polyamide 6 (PA 6)
Fillers Included: Glass Fiber
Processing Methods: Injection Molding
Note: ¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
Markets: Automotive & Transportation
Consumer Goods
Electrical & Electronics
Industrial
Technology: Plastics
Labeling Claims: No Added PFAS
Material Features: Heat Stabilized
High Stiffness
High Strength
Plastics and Elastomers End Uses: Automotive Applications
Commercial Appliance
Construction Applications
Home Appliances
Water Management
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 5

5 rows

Characteristic	Value	Unit	Method
Tensile Stress (Break) ¹	228.0	MPa	ASTM D638
Tensile Strain (Break) ¹	2.2	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹	17440.0	MPa	ASTM D638
Flexural Stress ¹	296.0	MPa	ASTM D790
Flexural Modulus ¹	15230.0	MPa	ASTM D790

Table 2 of 5

2 rows

Characteristic	Value	Unit	Method
Density ¹	1.61	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ²	0.2	%	ASTM D955

Table 3 of 5

1 row

Characteristic	Value	Unit	Method
Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹	205.0	°C	ASTM D648

Table 4 of 5