NORYL™ Resin TP0140IF

Chemical Family: PolyethersStyrenics

NORYL™ Resin TP0140IF is a non-reinforced blend of polyphenylene ether (PPE) and polystyrene (PS). This injection moldable grade is distinguished by its high transparency, excellent heat resistance, high ductility, minimal water absorption, and superior dimensional stability. NORYL™ Resin TP0140IF is compliant with FDA food contact regulations and does not intentionally contain PFAS or Bisphenol A. Ideal for a range of applications including small appliances, steamers, water bottles, cutlery, and other food contact uses, NORYL™ Resin TP0140IF offers manufacturers a reliable material choice that prioritizes safety, performance, and regulatory compliance in food-related applications.

Product families

Applications

Consumer Goods — Appliances & Electronics

Printing & Packaging — Packaging

Food & Beverage Packaging

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Other characteristics

Brand: NORYL™ Resin
Density: 1050.0 - 1050.0 kg/m³
Polymer Name: PPE/PS Alloy
Flexural Modulus: 2380.0 - 2380.0 MPa
Processing Methods: Injection Molding
Note: (1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. (2) Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. (3) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
Markets: Consumer Goods
Printing & Packaging
Technology: Plastics
Labeling Claims: Bisphenol A-free
Food Contact Acceptable
No Added PFAS
Material Features: Amorphous
Dimensional Stability
Excellent Transparency Properties
Food Contact Acceptable
Heat Resistance
High Ductility
High Hydrolytic Stability
Low Corrosion
Plastics and Elastomers End Uses: Commercial Appliance
Cutlery
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Injection Molding

Technical data

Table 1 of 6

14 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹	70.0	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹	48.0	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹	5.3	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹	15.0	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹	2280.0	MPa	ASTM D638
Flexural Strength (1.3 mm/min, 50 mm span) ¹	105.0	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹	2350.0	MPa	ASTM D790
Tensile Stress (Yield, 50 mm/min) ¹	73.5	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹	48.5	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹	5.1	%	ISO 527
Tensile Strain (Break, 50 mm/min) ¹	12.0	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹	2470.0	MPa	ISO 527

Table 2 of 6

5 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹	1.05	—	ASTM D792
Melt Flow Rate (at 300°C/5.0 kgf )¹	16.0	g/10 min	ASTM D1238
Water Absorption (23°C/24hrs) ¹	0.06	%	ISO 62-1
Mold Shrinkage (flow, 3.2 mm) ²	0.9 - 1.1	%	SABIC method
Mold Shrinkage (xflow, 3.2 mm) ²	1.0 - 1.2	%	SABIC method

Table 3 of 6

2 rows

Characteristic	Value	Unit	Method
Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹	139.0	°C	ASTM D648
Heat Deflection Temperature/Af (1.8 MPa Flatw 80104 sp=64mm) ¹	138.0	°C	ISO 75/Af

Table 4 of 6

3 rows

Characteristic	Value	Unit	Method
Light Transmission (at 2.0 mm) ¹	82.0	%	ASTM D1003
Haze (2mm) ¹	2.0	%	SABIC method
Yellowness Index ¹	45.0	—	ASTM D1925

Table 5 of 6