LNP™ VERTON™ Compound MV008SU
- Chemical Family
- PolyolefinsPolypropylenes (PP)
LNP™ VERTON™ Compound MV008SU integrates polypropylene (PP) resin with a robust 40% long glass fiber composition, enhancing structural integrity and stiffness. This compound is engineered with chemical coupling for optimized performance, along with heat and UV stabilization to ensure durability and weather resistance. It is tailored for demanding applications in automotive exteriors, building components, water management systems, sports and leisure equipment, as well as home and commercial appliances.
Product families
Applications
- Consumer Goods — Appliances & Electronics
- Consumer Goods — Sports & Recreation
- Exterior & Body
- Waterproofing & Weatherproofing
- Equipment & Parts
- Consumer Electronics
Product Families
- Polyolefins
Other characteristics
- Brand
- LNP™ VERTON™ Compound
- Polymer Name
- Polypropylene (unspecified)
- Fillers Included
- Glass Fiber, Long Glass Fiber
- Glass Fiber
- Long Glass Fiber
- Processing Methods
- Injection Molding
- Note
¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. ² Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article. ³ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Automotive & Transportation
- Building & Construction
- Consumer Goods
- Electrical & Electronics
- Industrial
- Technology
- Plastics
- Labeling Claims
- No Added PFAS
- Material Features
- Chemically Coupled
- Good UV Stability
- Good Weather Stability
- Heat Stabilized
- High Stiffness
- High Strength
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- Automotive Applications
- Commercial Appliance
- Construction Applications
- Home Appliances
- Water Management
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
10 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Break) ¹ | 119.0 | MPa | ASTM D638 |
| Tensile Stress (Break) ¹ | 127.0 | MPa | ISO 527 |
| Tensile Strain (Break) ¹ | 2.6 | % | ASTM D638 |
| Tensile Strain (Break) ¹ | 2.5 | % | ISO 527 |
| Tensile Modulus (at 50 mm/min) ¹ | 9550.0 | MPa | ASTM D638 |
| Flexural Stress ¹ | 179.0 | MPa | ASTM D790 |
| Flexural Stress ¹ | 187.0 | MPa | ISO 178 |
| Flexural Modulus ¹ | 7800.0 | MPa | ASTM D790 |
| Flexural Modulus ¹ | 8250.0 | MPa | ISO 178 |
| Tensile Modulus (at 1 mm/min) ¹ | 10120.0 | MPa | ISO 527 |
Table 2 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.23 | g/cm³ | ASTM D792 |
| Density ¹ | 1.22 | g/cm³ | ISO 1183 |
| Mold Shrinkage (flow, 24 hrs) ² | 0.1 | % | ASTM D955 |
| Mold Shrinkage (flow, 24 hrs) ² | 0.08 | % | ISO 294 |
| Mold Shrinkage (xflow, 24 hrs) ² | 0.3 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ² | 0.32 | % | ISO 294 |
Table 3 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature (1.82 MPa, 3.2mm, unannealed) ¹ | 157.0 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ | 4.6e-05 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹ | 4.61e-05 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ | 8.26e-05 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹ | 8.27e-05 | 1/°C | ISO 11359-2 |
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 164.0 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (1.8 MPa Flatw 80*10*4 sp=64mm) ¹ | 160.0 | °C | ISO 75/Af |
Table 4 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 23°C) ¹ | 208.0 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy (at peak, 23°C) ¹ | 10.0 | J | ASTM D3763 |
| Multiaxial Impact ¹ | 10.0 | J | ISO 6603 |
| Izod Impact (Unnotched 80*10*4 +23°C) ¹ | 50.0 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 25.0 | kJ/m² | ISO 180/1A |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ³ | 80.0 | °C |
| Drying Time ³ | 4.0 | Hrs |
| Melt Temperature ³ | 220 - 250 | °C |
| Front - Zone 3 Temperature ³ | 250 - 260 | °C |
| Middle - Zone 2 Temperature ³ | 245 - 255 | °C |
| Rear - Zone 1 Temperature ³ | 230 - 245 | °C |
| Mold Temperature ³ | 40 - 65 | °C |
| Back Pressure ³ | 0.2 - 0.3 | MPa |
| Screw Speed ³ | 30 - 60 | rpm |