NORYL™ Resin WM300G
- Chemical Family
- PolyethersStyrenics
NORYL™ Resin WM300G is a non-reinforced, impact-modified blend of Polyphenylene ether (PPE) and polystyrene (PS). This resin is noted for its superior surface appearance, high ductility, low moisture absorption, and exceptional dimensional and hydrolytic stability. The use of specialized impact modification ensures improved processing stability, minimizing the risk of restricted substance formation during processing. NORYL™ Resin WM300G is ideally suited for a range of water management applications, including valves, filtration components, and water meter internals. It can be processed via injection molding and extrusion (e.g., pipe and profile applications).
Product families
Applications
- Pipes & Plumbing
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ Resin
- Density
- 1060.0 - 1060.0 kg/m³
- Polymer Name
- PPE/PS Alloy
- Flexural Modulus
- 2500.0 - 2500.0 MPa
- Processing Methods
- Extrusion, Injection Molding
- Note
(1) The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design. (2) Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- Markets
- Building & Construction
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- No Added PFAS
- Material Features
- Amorphous
- Dimensional Stability
- Food Contact Acceptable
- Good Surface Appearance
- High Ductility
- High Hydrolytic Stability
- High Stiffness
- High Strength
- Plastics and Elastomers End Uses
- Filtration Plates
- Potable Water Applications
- Valves
- Water Management
- Water Meter Gear
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Extrusion
- Injection Molding
Technical data
Table 1 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Modulus (at 1 mm/min) ¹ | 2500.0 | MPa | ISO 527 |
| Tensile Stress (Yield, 50 mm/min) ¹ | 65.0 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹ | 52.0 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹ | 4.5 | % | ISO 527 |
| Flexural Strength (2 mm/min) ¹ | 100.0 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹ | 2500.0 | MPa | ISO 178 |
Table 2 of 6
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹ | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume Rate (at 300°C/5.0 kg) ¹ | 15.0 | cm³/10 min | ISO 1133 |
| Mold Shrinkage (flow) ¹ | 0.8 - 1 | % | SABIC method |
| Mold Shrinkage (xflow) ¹ | 0.8 - 1 | % | SABIC method |
| Moisture Absorption (23°C / 50% RH) ¹ | 0.06 | % | ISO 62 |
| Water Absorption (23°C/saturated) ¹ | 0.23 | % | ISO 62-1 |
Table 3 of 6
2 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Heat Deflection Temperature/Bf (0.45 MPa Flatw 80*10*4 sp=64mm) ¹ | 147.0 | °C | ISO 75/Bf |
| Vicat Softening Temperature (at Rate B/120) ¹ | 155.0 | °C | ISO 306 |
Table 4 of 6
12 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature | 100 - 120 | °C |
| Drying Time | 2 - 3 | Hrs |
| Melt Temperature | 220 - 285 | °C |
| Barrel - Zone 1 Temperature | 220 - 285 | °C |
| Barrel - Zone 2 Temperature | 220 - 285 | °C |
| Barrel - Zone 3 Temperature | 220 - 285 | °C |
| Barrel - Zone 4 Temperature | 220 - 285 | °C |
| Hopper Temperature | 60 - 80 | °C |
| Adapter Temperature | 220 - 285 | °C |
| Die Temperature | 220 - 285 | °C |
| Calibrator Temperature | 30 - 60 | °C |
| Water Bath Temperature | 30 - 50 | °C |
Table 5 of 6
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched 80*10*4 +23°C) ¹ | 18.0 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched 80*10*4 0°C) ¹ | 12.0 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹ | 20.0 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 0°C, V-notch Edgew 80*10*4 sp=62mm) ¹ | 14.0 | kJ/m² | ISO 179/1eA |
Table 6 of 6
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ² | 100 - 120 | °C |
| Drying Time ² | 2 - 3 | Hrs |
| Melt Temperature ² | 280 - 330 | °C |
| Rear - Zone 1 Temperature ² | 240 - 290 | °C |
| Middle - Zone 2 Temperature ² | 260 - 310 | °C |
| Front - Zone 3 Temperature ² | 280 - 330 | °C |
| Nozzle Temperature ² | 260 - 330 | °C |
| Mold Temperature ² | 80 - 120 | °C |
| Hopper Temperature ² | 60 - 80 | °C |