LNP™ ELCRES™ DMX1435D

Chemical Family: Polycarbonate (PC)

SABIC's Specialties Business LNP ELCRES DMX1435D is a UV stabilized standard flow Polycarbonate (PC) copolymer resin with diffusion effect and improved scratch resistance. This grade is a good candidate for consumer electronics, mobility interiors and other adjacent applications, which need lower scratch and diffusive effects performance.

Product families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics
Polycarbonates

Other characteristics

Brand: LNP™ ELCRES
Polymer Name: Polycarbonate (PC)
Flexural Modulus: 2600.0 - 2600.0 MPa
Additives Included: UV Stabilizer
Processing Methods: Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Translucent
Transparent
Markets: Automotive & Transportation
Building & Construction
Consumer Goods
Electrical & Electronics
Healthcare & Pharma
Flame Rating: UL 94 HB
Technology: Plastics
Material Features: Good Aesthetics
Good Scratch Resistance
Good Surface Appearance
Good UV Stability
Good Weather Stability
IR Transparent
Translucent
UV Resistant
Country Availability: China (Mainland)
Certifications and Compliance: UL 94
Plastics and Elastomers End Uses: Air Conditioner
Audio Equipment
Automotive Applications
Automotive Exterior Parts
Automotive Interior Parts
Building Materials
Bus
Cell Phones

Technical data

Table 1 of 7

17 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	77	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	60	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	7.5	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	20	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2700	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	120	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2500	MPa	ASTM D790
Hardness (Rockwell L) ¹¹	110	—	ASTM D785
Hardness (Rockwell M) ¹¹	90	—	ASTM D785
Tensile Stress (Yield, 50 mm/min) ¹¹	77	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	59	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	7	%	ISO 527

Table 2 of 7

13 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.18	—	ASTM D792
Specific Volume ¹¹	0.85	cm³/g	ASTM D792
Density ¹¹	1.18	g/cm³	ISO 1183
Density ¹¹	1.17	g/cm³	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.08	%	ASTM D570
Water Absorption (at 23°C, saturated) ¹¹	0.28	%	ASTM D570
Water Absorption (at 23°C, saturated) ¹¹	0.27	%	ISO 62-1
Moisture Absorption (at 50% RH, Equilibrium) ¹¹	0.13	%	ASTM D570
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.04	%	ASTM D570
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.5 - 0.8	%	SABIC method
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	15.4	g/10 min	ASTM D1238
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.13	%	ISO 62

Table 3 of 7

14 rows

Characteristic	Value	Unit	Method
Vicat Softening Temperature (Rate B/50) ¹¹	136	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	138	°C	ASTM D1525
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	129	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	115	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹	0.00007	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 95°C, xflow) ¹¹	0.00007	1/°C	ASTM E831
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹	0.00007	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹	0.00007	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate B/120) ¹¹	138	°C	ISO 306
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	129	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	115	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B

Table 4 of 7

2 rows

Characteristic	Value	Unit	Method
Light Transmission (at 2.0 mm) ¹¹	85	%	ASTM D1003
Haze (at 2 mm) ¹¹	85	%	SABIC method

Table 5 of 7

12 rows

Characteristic	Value	Unit	Method
Izod Impact (Unnotched, at 23°C) ¹¹	No break	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	30	J/m	ASTM D256
Izod Impact (Notched, at -30°C) ¹¹	30	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	7	J	ASTM D3763
Izod Impact (Unnotched, 80103, at 23°C) ¹¹	No break	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80103, at -30°C) ¹¹	40	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80103, at 23°C) ¹¹	2.2	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80103, at -30°C) ¹¹	2	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80103 sp=62mm) ¹¹	2.2	kJ/m²	ISO 179/1eA
Charpy Impact (at -30°C, V-notch Edgew 80103 sp=62mm) ¹¹	2.5	kJ/m²	ISO 179/1eA
Charpy Impact (at 23°C, Unnotch Edgew 80103 sp=62mm) ¹¹	No break	kJ/m²	ISO 179/1eU
Charpy Impact (at -30°C, Unnotch Edgew 80103 sp=62mm) ¹¹	46	kJ/m²	ISO 179/1eU

Table 6 of 7

10 rows

Characteristic	Value	Unit
Drying Temperature ⁷	120	°C
Drying Time ⁷	3 - 4	Hrs
Maximum Moisture Content ⁷	0.02	%
Melt Temperature ⁷	295 - 315	°C
Nozzle Temperature ⁷	290 - 310	°C
Front - Zone 3 Temperature ⁷	295 - 315	°C
Middle - Zone 2 Temperature ⁷	280 - 305	°C
Rear - Zone 1 Temperature ⁷	260 - 280	°C
Hopper Temperature ⁷	60 - 80	°C
Mold Temperature ⁷	70 - 95	°C

Table 7 of 7

1 row

Characteristic	Value	Unit	Method
UL Recognized (94HB Flame Class Rating) ᵖ	min. 0.6	mm	UL 94