NORYL™ PPE 6850C
SABIC's Specialties Business NORYL™ 6850C resin concentrate is an non-reinforced blend of polyphenylene ether (PPE) + general purpose polystyrene (GPPS). This material is in granule form and is optimized for blending with polystyrene resins. NORYL™ 6850C resin may be an excellent candidate in microwavable food packaging applications and is compliant with US and European food contact regulations This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.
Product families
Applications
- Electrical & Electronic Systems
- Food & Beverage Packaging
- Industrial & Transport Packaging
- Non-Food Consumer Packaging
- Batteries
- Housings & Enclosures
Product Families
- Blends & Alloys
Other characteristics
- Brand
- NORYL™ PPE
- Density
- 1060.0 - 1060.0 kg/m³
- Polymer Name
- PPE/GPPS Alloy
- Flexural Modulus
- 2580.0 - 2580.0 MPa
- Processing Methods
- Injection Molding
- Note
⁷ Параметры литья под давлением упоминаются только в качестве общих рекомендаций. Они могут не применяться или требовать корректировки в конкретных ситуациях, таких как малые объемы впрыска, литье крупногабаритных деталей, литье тонкостенных деталей и газовое литье.. ¹¹ Информация, указанная в технических паспортах, должна использоваться только в качестве ориентировочной для целей выбора материала и не должна использоваться в качестве спецификации или для проектирования деталей или пресс-форм.
- Color
- Translucent
- Transparent
- Markets
- Automotive & Transportation
- Electrical & Electronics
- Printing & Packaging
- Flame Rating
- UL 94 V0
- Technology
- Plastics
- Labeling Claims
- Food Contact Acceptable
- No Added PFAS
- Material Features
- Amorphous
- Creep Resistant
- Dimensional Stability
- Food Contact Acceptable
- Good Stiffness
- High Hydrolytic Stability
- High Stiffness
- High Tensile Strength
- Certifications and Compliance
- UL 94
- Plastics and Elastomers End Uses
- 3D Printing Applications
- Battery Cases
- Bottom Enclosure
- Circuit Board
- Consumer Applications
- EV Battery Modules
- Electrical Enclosure
- Electrical Internal Frame
- Plastics and Elastomers Functions
- Resin
- Plastics and Elastomers Processing Methods
- Injection Molding
Technical data
Table 1 of 5
7 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Tensile Stress (Yield, 50 mm/min) ¹¹ | 70 | MPa | ISO 527 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 70 | MPa | ISO 527 |
| Tensile Strain (Yield, 50 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 5 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 2540 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 107 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2580 | MPa | ISO 178 |
Table 2 of 5
5 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Density ¹¹ | 1.06 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.25 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.06 | % | ISO 62 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 40 | cm³/10 min | ISO 1133 |
| Melt Viscosity (at 280°C, 1500 sec⁻¹) ¹¹ | 133 | Pa-s | ISO 11443 |
Table 3 of 5
6 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate A/120) ¹¹ | 151 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 143 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 145 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 125 | °C | ISO 75/Af |
Table 4 of 5
4 rows| Characteristic | Value | Unit | Method |
|---|---|---|---|
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 4 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 2 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 4 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 3 | kJ/m² | ISO 179/1eA |
Table 5 of 5
9 rows| Characteristic | Value | Unit |
|---|---|---|
| Drying Temperature ⁷ | 80 - 100 | °C |
| Drying Time ⁷ | 2 - 4 | Hrs |
| Melt Temperature ⁷ | 280 - 300 | °C |
| Nozzle Temperature ⁷ | 260 - 280 | °C |
| Front - Zone 3 Temperature ⁷ | 280 - 300 | °C |
| Middle - Zone 2 Temperature ⁷ | 260 - 280 | °C |
| Rear - Zone 1 Temperature ⁷ | 240 - 260 | °C |
| Hopper Temperature ⁷ | 60 - 80 | °C |
| Mold Temperature ⁷ | 60 - 100 | °C |