LNP™ COLORCOMP™ Compound W1000PRB

Chemical Family: Polyesters

SABIC's Specialties Business LNP COLORCOMP W1000PRB compound is based on Polybutylene Terephthalate (PBT) resin. Added features of this grade include: Healthcare, Food Contact Compliant, Biocompatible (ISO 10993 or USP Class VI), EtO and Gamma Sterilizable, Mold Release. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product families

Applications

Consumer Goods — Appliances & Electronics

Electrical & Electronics — Devices & Assemblies

Consumer Electronics

Healthcare & Pharma — Medical

Medical Devices & Assemblies
Surgical Instruments & Trays
Tubing & Fluids Handling

Printing & Packaging — Packaging

Food & Beverage Packaging
Healthcare Packaging
Industrial & Transport Packaging
Non-Food Consumer Packaging

Product Families

Plastics — Engineering & Specialty Polymers

Polyesters & Copolyesters

Other characteristics

Brand: LNP™ COLORCOMP™ Compound
Polymer Name: Polybutylene Terephthalate (PBT)
Flexural Modulus: 2260.0 - 2260.0 MPa
Additives Included: Mold Release Agent
Processing Methods: Compounding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.; ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.; ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Color: Custom
Transparent
Markets: Consumer Goods
Electrical & Electronics
Healthcare & Pharma
Printing & Packaging
Technology: Plastics
Labeling Claims: Biocompatible
Food Contact Acceptable
No Added PFAS
Material Features: Biocompatible
E-Beam Sterilizable
Ethylene Oxide Sterilizable
Excellent Aesthetics
Food Contact Acceptable
Gamma Sterilizable
Good Aesthetics
Good Mold Release
Certifications and Compliance: ISO 10993
USP Class VI
Plastics and Elastomers End Uses: Appliances
Consumer Applications
Fluid Handling
Food Packaging
Home Appliances
Medical Devices
Medical Packaging
Medical/Healthcare Applications
Plastics and Elastomers Functions: Resin
Plastics and Elastomers Processing Methods: Compounding

Technical data

Table 1 of 6

14 rows

Characteristic	Value	Unit	Method
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	60	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	26	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	3.7	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	10	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	2700	MPa	ASTM D638
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	89	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2500	MPa	ASTM D790
Tensile Stress (Yield, 50 mm/min) ¹¹	50	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	49	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	3.2	%	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	10	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2600	MPa	ISO 527

Table 2 of 6

7 rows

Characteristic	Value	Unit	Method
Specific Gravity ¹¹	1.31	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	1.5 - 2	%	SABIC method
Melt Flow Rate (at 265°C, 2.16kgf) ¹¹	80	g/10 min	ASTM D1238
Density ¹¹	1.31	g/cm³	ISO 1183
Water Absorption (at 23°C, saturated) ¹¹	0.4	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.08	%	ISO 62
Melt Volume Rate (at 265°C, 2.16 kg) ¹¹	70	cm³/10 min	ISO 1133

Table 3 of 6

10 rows

Characteristic	Value	Unit	Method
Vicat Softening Temperature (Rate B/50) ¹¹	183	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	180	°C	ASTM D1525
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	150	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	54	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000076	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000076	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000078	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000078	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate B/120) ¹¹	180	°C	ISO 306
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	49	°C	ISO 75/Af

Table 4 of 6

6 rows

Characteristic	Value	Unit	Method
Izod Impact (Notched, at 23°C) ¹¹	30	J/m	ASTM D256
Izod Impact (Notched, at -30°C) ¹¹	30	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	20	J	ASTM D3763
Izod Impact (Notched, 80104, at 23°C) ¹¹	2	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at -30°C) ¹¹	2	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80104 sp=62mm) ¹¹	6	kJ/m²	ISO 179/1eA

Table 5 of 6